Method for forming carbide banding in steel materials using deformation
OwnerDaniel Watsoninventor
Life of this patent
Estimating the term…
Abstract
The method of making steel with carbide banding entails using steel with undissolved carbides distributed within the steel for forming steel with carbide banding, wherein the steel is about 0.3 weight percent to about 2.2 weight percent carbon and at least 0.003 weight percent of chromium, molybdenum, aluminum, vanadium, tungsten, or a similar carbide forming element; then, deforming the steel with undissolved carbides to create steel with carbide banding upon cooling, heating the steel with undissolved carbides for a specified time ranging at a specified temperature to form an austenitic steel with undissolved carbides, and cooling the austenitic steel with undissolved carbides to maintain the undissolved carbides within a crystalline matrix forming steel with carbide banding.
Claims22
A method of making steel with carbide banding comprising the steps of:
- a. obtaining steel with undissolved carbides distributed within the steel for forming steel with carbide banding, wherein the steel comprises:
- i. from about 0.3 weight percent to about 2.2 weight percent carbon;
- and
- ii. at least about 0.003 weight percent of a metal selected from the group consisting of chromium, molybdenum, aluminum, vanadium, or tungsten;
- b. deforming the steel with undissolved carbides to create steel with carbide banding upon cooling;
- c. heating the steel with undissolved carbides for a time ranging from about 5 minutes to about 12 hours at a temperature above an A-sub 1 temperature to form an austenitic steel with undissolved carbides;
- and
- d. cooling the austenitic steel with undissolved carbides to maintain the undissolved carbides within a crystalline matrix forming steel with carbide banding.
A method of making steel with carbide banding, comprising the steps of:
- a. obtaining steel without dissolved carbides, wherein the steel comprises:
- i. from about 0.3 weight percent to about 2.2 weight percent carbon;
- and
- ii. at least about 0.003 weight percent of a metal selected from the group consisting of chromium, molybdenum, aluminum, vanadium, or tungsten;
- b. forming carbides in the steel by heating the steel without dissolved carbides at a temperature in the range from about an A-sub 1 temperature to about 50 degrees Fahrenheit below an A-sub 3 temperature for a time ranging from 10 minutes to 12 hours to form an austenitic steel with undissolved carbides;
- c. deforming the austenitic steel with undissolved carbides;
- and
- d. cooling the austenitic steel to precipitate carbides within a crystalline matrix forming a steel with carbide banding.
A method of making steel with carbide banding, comprising the steps of:
- a. obtaining steel without dissolved carbides, wherein the steel comprises:
- i. from about 0.3 weight percent to about 2.2 weight percent carbon;
- and
- ii. at least about 0.003 weight percent of a metal selected from the group consisting of chromium, molybdenum, aluminum, vanadium, or tungsten;
- b. forming carbides in the steel by heating the steel without dissolved carbides at a temperature just below an A-sub 1 temperature to form an austenitic steel with undissolved carbides;
- c. holding the heated austenitic steel with undissolved carbides at the temperature just below the A-sub 1 temperature for a time ranging from about 10 minutes to about 12 hours to form carbides in the steel;
- d. deforming the steel with formed carbides;
- and
- e. cooling the steel with formed carbides to precipitate the formed carbides within a crystalline matrix forming a steel with carbide banding.
A method of making steel with carbide banding, comprising the steps of:
- a. obtaining steel without dissolved carbides, wherein the steel comprises:
- i. from about 0.3 weight percent to about 2.2 weight percent carbon;
- and
- ii. at least about 0.003 weight percent of a metal selected from the group consisting of chromium, molybdenum, aluminum, vanadium, or tungsten;
- b. forming carbides in the steel by cyclically heating the steel without carbides at a temperature just above an A-sub 1 temperature and just below an A-sub 3 temperature to form an austenitic steel with undissolved carbides;
- c. deforming the steel with formed carbides;
- and
- d. cooling the steel with formed carbides to precipitate the formed carbides within a crystalline matrix forming a steel with carbide banding.
A method of making steel with carbide banding, comprising the steps of:
- a. obtaining steel without carbides, wherein the steel comprises:
- i. from about 0.3 weight percent to about 2.2 weight percent carbon;
- and
- ii. at least about 0.003 weight percent of a metal selected from the group consisting of chromium, molybdenum, aluminum, vanadium, or tungsten;
- b. deforming the steel to create carbide banding;
- c. forming carbides in the steel, comprising the steps of:
- i. heating the steel without carbides to a temperature just below an A-sub 1 temperature;
- and
- ii. holding the heated steel at that temperature just below an A-sub 1 temperature for a time ranging from about 10 minutes to about 12 hours thereby forming carbides in the steel;
- d. heating the steel with formed carbides for a time less than about 5 minutes at a temperature above an A-sub 3 temperature forming an austenitic steel with undissolved carbides;
- and
- e. cooling the austenitic steel with undissolved carbides to maintain the undissolved carbides within a chosen crystalline matrix forming a steel with carbide banding.
Dependencies are inferred from the claim text.