# US 7,407,704 B2 · Process for adhesive separation of bonded joints > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 7,407,704 B2 - Document ID: US7407704B2 - Status: Granted - Kind: B2 - Application number: 10/930,571 - Filed: 2004-08-31 - Published: 2005-02-24 - Granted: 2008-08-05 - Earliest claimed: 1999-10-27 - Assignees: Henkel AG & Co. KGaA - Inventors: Christian Kirsten - Web page: https://patentgrep.com/patent/US7407704B2 ## CPC - C09J 5/02: involving pretreatment of the surfaces to be joined - C09J 5/06: involving heating of the applied adhesive - C09J 9/00: Adhesives characterised by their physical nature or the effects produced, e.g. glue sticks (C09J7/00 takes precedence) - C09J 11/04: inorganic - C09J 2301/502: process for debonding adherents - Y10T 156/1153: Temperature change for delamination [e.g., heating during delaminating, etc.] - Y10T 428/25: Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles - Y10T 428/256: Heavy metal or aluminum or compound thereof - Y10T 428/258: Alkali metal or alkaline earth metal or compound thereof - C09J: ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES (preparation of glue or gelatine C09H) - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract The reversible separation of bonded joints by applying alternating electromagnetic fields is described. The bonded joint consists of at least one primer layer which contains nanoscale particles which have ferromagnetic, ferrimagnetic, superparamagnetic or piezoelectric properties. As a result of the alternating electromagnetic fields, large amounts of localised heat are produced in the primer layer of the bonded joint. This localised heat input causes, in the case of adjacent thermoplastic adhesive layers, softening of the thermoplastic binder. If thermoset adhesives are adjacent to the boundary layer of the primer, then the cross-linked structure in the binder matrix is broken up due to the high degree of localised warming. In both cases quasi-adhesive substrate separation with a low energy input is enabled as a result of the high localised warming of the boundary layer. ## Claims ### Claim 1 A separable bonded joint comprising an electromagnetically activatable primer layer and an adhesive layer adjacent to the primer layer, wherein the primer layer contains nanoscale particles with ferromagnetic, ferrimagnetic, superparamagnetic or piezoelectric properties. ### Claim 2 An assembly of two or more substrates separably bonded in at least a friction-tight bond by a bonded joint between the substrates comprising a primer layer and an adhesive layer, wherein the primer comprises nanoscale particles with ferromagnetic, ferrimagnetic, superparamagnetic or piezoelectric properties. ### Claim 3 (depends on 2) The assembly of claim 2, wherein said primer is heatable by application of an alternating electromagnetic field. ### Claim 4 (depends on 2) The assembly of claim 2, wherein the nanoscale particles have an average particle size of less than of equal to 200 nm. ### Claim 5 (depends on 4) The assembly of claim 4, wherein the nanoscale particles have an average particle size of less than or equal to 100 nm. ### Claim 6 (depends on 5) The assembly of claim 5, wherein the nanoscale particles have an average particle size of less than or equal to 50 nm. ### Claim 7 (depends on 2) The assembly of claim 2, wherein the nanoscale particles comprise one or more piezoelectric substances selected from the group consisting of quartz, tourmaline, barium titanate, lithium sulfate, potassium tartrate, sodium tartrate, potassium sodium tartrate, ethylenediamine tartrate, ferroelectric compounds with a Perovskite structure, and lead zirconium titanate. ### Claim 8 (depends on 2) The assembly of claim 2, wherein the nanoscale particles comprise one or more ferromagnetic, ferrimagnetic or superparamagnetic substances selected from the group consisting of aluminum, cobalt, iron, nickel and their alloys, metal oxides of the n-maghemite (γ-Fe2O3) and n-magnetite (Fe3O4) type, and ferrites of the MeFe2O4type, wherein Me represents a divalent metal selected from manganese, copper, zinc, cobalt, nickel, magnesium, calcium, and cadmium. ### Claim 9 (depends on 2) The assembly of claim 2, wherein said primer comprises 1% to 30% by weight of the nanoscale particles. ### Claim 10 (depends on 9) The assembly of claim 9, wherein said primer comprises 2% to 20% by weight of the nanoscale particles. ### Claim 11 (depends on 2) The assembly of claim 2, wherein said adhesive layer comprises a thermoplastic adhesive layer. ### Claim 12 (depends on 2) The assembly of claim 2, wherein said adhesive layer comprises a thermoset adhesive layer. ### Claim 13 (depends on 2) The assembly of claim 2, wherein said adhesive layer is free of said nanoscale particles. ### Claim 14 (depends on 2) The assembly of claim 2, wherein said primer layer is between the adhesives layer and at least one of the substrates. ### Claim 15 (depends on 2) The assembly of claim 2, wherein said bonded joint between the substrates further comprises a second primer layer, said adhesive layer spacing first and second primer layer. ### Claim 16 (depends on 2) A process for loosening the bonded joint of the assembly of claim 2, comprising subjecting the primer layer to an alternating electric, magnetic or electromagnetic field, wherein the primer layer is locally heated, whereby said bonded joint is separable. ### Claim 17 (depends on 16) The process of claim 16, wherein said adhesive layer comprises a thermoplastic adhesive layer and said adhesive layer had a boundary layer in contact with the primer layer, the boundary layer being heated by the primer layer to above the softening point of the thermoplastic adhesive, whereby the substrates can be separated. ### Claim 18 (depends on 16) The process of claim 16, wherein said adhesive layer comprises a thermoset adhesive layer and said adhesive layer has a boundary layer in contact with the primer layer, the boundary layer being heated by the primer layer to a temperature that breaks the cross-linked thermoset structure whereby the substrates can be separated. ### Claim 19 (depends on 2) A process of forming the assembly of claim 2, comprising applying the primer layer between the adhesive layer and at least one of the substrates.