Shutdown separators with improved properties

Abstract

A microporous polyolefin battery separator membrane is extremely high in porosity, high in puncture strength, very low in shrinkage and with shutdown temperature of 130-140 degrees C. and melt integrity greater than 165 degrees C. It is made of UHMWPE having a weight-average molecular weight of 1×106 or more and an inert filler. A second microporous polyolefin battery separator has a shutdown temperature of between 95 and 110 degrees C. and a melt integrity of more than 165 degrees C. It is made from an UHMWPE having a weight-average molecular weight of 1×106 or more, a shutdown (LMWPE) having a weight-average molecular weight of 4500 or less and an inert filler. Both membranes have a thickness of 5-75 microns, a porosity of 30-95%, an air permeability of 1-200 sec/10 cc, an average pore diameter of 0.001 to 1 micron and puncture strength of more than 300 grams/25 μm.