Current fuse and method of making the current fuse
AssigneeKoa Corporation
InventorsSatoru Kobayashi, Kazuyuki Kato
Life of this patent
Estimating the term…
Abstract
In order to provide a current fuse with high solderability without containing harmful materials, solder chips containing 30 to 60 percent by weight of zinc, 0.1 to 2 percent by weight of copper, 0.1 to 1 percent by weight of nickel, and the remainder percent by weight being tin, or further containing 0.01 to 0.5 percent by weight of aluminum are inserted into the interior of the electrodes before pressing the electrodes into the ends of the substrate of the fuse, the exterior of the electrodes is heated to melt the solder chips, thereby connecting between the electrodes and the fuse wire.
Claims4
A current fuse comprising a fuse wire and electrodes, said fuse wire being connected to said electrodes by a lead-free solder, wherein
- said lead-free solder comprising at least 30 to 60 percent by weight of zinc, 0.1 to 2 percent by weight of copper, 0.1 to 1 percent by weight of nickel, with the remainder percent by weight being tin.
A current fuse, comprising:
- a fuse wire;
- a container for said fuse wire;
- cap electrodes that are disposed on both ends of said container;
- and
- a lead-free solder is disposed between said fuse wire and said cap electrodes, and
- said lead-free solder comprising at least 30 to 60 percent by weight of zinc, 0.1 to 2 percent by weight of copper, 0.1 to 1 percent by weight of nickel, with the remainder percent by weight being tin.
Dependencies are inferred from the claim text.