Composite oxide, process for producing the same, and exhaust gas reducing co-catalyst

Abstract

A composite oxide includes CeO2, ZrO2 and a metallic oxide being free from reacting with CeO2 and ZrO2 at 700° C. or more, preferably at 900° C. or more and further preferably at 1,000° C. or more. The composite oxide has a regulatory oriented phase, such as a pyrochlore phase, etc., in which at least a part of Ce cations and Zr cations are oriented regularly. The composite oxide makes a catalytic support. The CeO2—ZrO2 composite oxide and the reaction-free metallic oxide make barriers each other which suppress the granular growth when the composite oxide is subjected to high-temperature heat in a reducing heat treatment to form the regulatory oriented phase. The regulatory oriented phase improves the oxygen storage-and-release capability of the catalytic support. Thus, it is possible to simultaneously attain a large a specific surface area and a high oxygen storage-and-release capability.