Composition for controlling spangle size, a coated steel product, and a coating method
AssigneeISG Technologies Inc.
InventorsErin T. McDevitt, Fritz J. Friedersdorf, H. E. George Rommal
Life of this patent
Estimating the term…
Abstract
A method of coating of steel products such as plate and sheet using an aluminum-zinc coating alloy includes modifying the coating bath with a particulate compound constituent in effective amounts to control the spangle facet size of the coated product, improve tension bend rust stain performance, and improve coated product paintability. Constituents include borides such as titanium boride and aluminum borides, carbides such as titanium carbide, and aluminides such as titanium aluminide. The method produces a coated steel product that does not require temper rolling for painting.
Claims44
In a coated steel article comprising a steel substrate;
- and an aluminum-zinc coating thereon, the improvement comprising said aluminum-zinc coating modified with an effective amount of one or more of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium, a boride compound containing aluminum, an aluminide compound containing titanium, an aluminide compound containing iron, a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, said aluminum-zinc coating having a spangle facet size of about 0.5 mm and smaller.
In an aluminum-zinc steel product coating composition containing between about 25% and 70% by weight aluminum, the improvement comprising the aluminum-zinc alloy including an effective amount of one or more of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of titanium boride a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, whereby said selected constituent particles provide a facet size of about 0.5 mm and smaller when the aluminum-zinc alloy is applied as a coating to the steel product.
In a coated steel article comprising a steel substrate;
- and an aluminum-zinc coating thereon, the improvement comprising the aluminum-zinc coating modified with an effective amount of one or more of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium, a boride compound containing aluminum, an aluminide compound containing titanium, an aluminide compound containing iron, a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, whereby when the particulate compound constituent is said boride compound, said modified coating is applied to the article in an aluminum-zinc alloy bath having a mass Z, said bath including an aluminum master alloy addition having a mass Y and a weight fraction X of said boride compound so that when said master alloy is added to said aluminum-zinc alloy bath in an amount calculated with the following equation
- X
- ×
- Y
- Z
- +
- Y
- =
- W
-
-
- where
-
-
- X
- >
- W
- so that an effective amount W comprising between about 0.001% to about 0.5% by weight boron is present in said boride compound in said modified coating, said modified coating having a spangle facet size between about 0.05 mm and 0.5 mm.
In an aluminum-zinc steel product coating composition containing between about 25% and 70% by weight aluminum, the improvement comprising the aluminum-zinc alloy including an effective amount of one or more of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of titanium boride, a carbide, compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, whereby when the particulate compound constituent is said titanium boride compound, said improved aluminum-zinc alloy is applied to the product in an aluminum-zinc coating bath having a mass Z, said bath including an aluminum master alloy addition having a mass Y and a weight fraction X of said titanium boride compound so that when said master alloy is added to said aluminum-zinc coating bath in an amount calculated with the following equation
- X
- ×
- Y
- Z
- +
- Y
- =
- W
-
-
- where
-
-
- X
- >
- W
- an effective amount W comprising between about 0.001% to about 0.5% by weight boron is present in said titanium boride compound in said improved alloy, whereby said titanium boride particles provide a spangle facet size between about 2.0 mm when W is about 0.001% boron by weight and 0.05 mm when W is about 0.5% boron by weight when the aluminum-zinc coating composition is applied to the steel product.
In a coated steel article comprising a steel substrate;
- and an aluminum-zinc coating thereon, the improvement comprising the aluminum-zinc coating modified with an effective amount of at least one particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium and a boride compound containing aluminum, whereby said aluminum-zinc coating has a spangle facet size of about 0.5 mm and smaller.
In a coated steel article comprising a steel substrate;
- and an aluminum-zinc coating thereon, the improvement comprising the aluminum-zinc coating modified with an effective amount of at least one particulate compound constituent having a particle size between about 0.01 microns and 25 microns, said particulate compound constituent selected from the group consisting of an aluminide compound containing titanium and an aluminide compound containing iron, whereby said aluminide particles provide improved spangle facet size reduction having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent in the aluminum-zinc coating.
In a coated steel article comprising a steel substrate;
- and an aluminum-zinc coating thereon, the improvement comprising the aluminum-zinc coating modified with an effective amount of at least one particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, whereby said carbide particles provide a spangle facet size of about 0.5 mm and smaller in the aluminum-zinc coating.
In an aluminum-zinc steel product coating composition having an aluminum content between 25% and 70% aluminum by weight, the improvement comprising the aluminum-zinc alloy including an effective amount of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent consisting of a boride compound containing titanium, whereby said boride compound particles provide a spangle facet size of about 0.5 mm and smaller when the aluminum-zinc alloy and said boride particles are applied to the steel product as a coating.
In an aluminum-zinc steel product coating composition having an aluminum content between 25% and 70% aluminum by weight, the improvement comprising the aluminum-zinc alloy including an effective amount of at least one particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, whereby said carbide compound particles provide a spangle facet size of about 0.5 mm and smaller when the aluminum-zinc alloy and said carbide particles are applied to the steel product as a coating.
In a method of coating a steel product using a molten aluminum-zinc alloy bath having an aluminum content between about 25% and 70% aluminum by weight, the improvement comprising:
- a) selecting a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium, a boride compound containing aluminum, an aluminide compound containing titanium, and aluminide compound containing iron, a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten;
- b) adding an effective amount of one or more of said selected constituent particles to the coating bath;
- c) applying said molten coating bath containing the molten aluminum-zinc along with said constituent particles to the steel product;
- and
- d) solidifying the molten aluminum-zinc, said constituent particles providing improved spangle facet size of about 0.5 mm and smaller during solidification.
In a method of coating a steel product using a molten aluminum-zinc alloy bath, the improvement comprising modifying the composition of the aluminum-zinc alloy by adding an effective amount of one or more of a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium, a boride compound containing aluminum, an aluminide compound containing titanium, an aluminide compound containing iron, a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten, said coating having a spangle facet size of about 0.5 mm and smaller, wherein when the particulate compound constituent is a boride compound, the steps of the method comprise:
- a) making an aluminum master alloy bath;
- b) adding said boride compound to the master alloy bath in an amount so that said master alloy bath comprises a weight fraction X of boride particulate compound;
- and
- c) adding said master alloy bath having a mass Y to the aluminum-zinc alloy bath having a mass Z in an amount calculated with the following equation
- X
- ×
- Y
- Z
- +
- Y
- =
- W
-
-
- where
-
-
- X
- >
- W
- so that an effective amount W comprising between about 0.001% to about 0.5% by weight boron is present in said particulate compound in the aluminum-zinc alloy bath.
In a method of coating a steel product using a molten aluminum-zinc alloy bath having an aluminum content between about 25% and 70% aluminum by weight, the improvement comprising modifying the composition of the aluminum-zinc alloy by:
- a) selecting a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a boride compound containing titanium and a boride compound containing aluminum;
- b) adding an effective amount of at least one selected boride compound to the coating bath;
- d) applying the molten aluminum-zinc alloy along with said boride compound particles to the steel product;
- and
- c) solidifying the aluminum-zinc alloy, said boride compound particles providing a spangle facet size of 0.5 mm and smaller.
In a method of coating a steel product using a molten aluminum-zinc alloy bath having an aluminum content between about 25% and 70% aluminum by weight, the improvement comprising modifying the composition of the aluminum-zinc alloy by:
- a) selecting a particulate compound constituent having a particle size between about 0.01 microns and 25 microns, said particulate compound constituent selected from the group consisting of an aluminide compound containing titanium and an aluminide compound containing iron;
- b) adding an effective amount of at least one selected aluminide compound to the bath so that the bath comprises the molten aluminum-zinc alloy and particles of said aluminide compound;
- e) applying the molten aluminum-zinc alloy and said aluminide compound particles to the steel product;
- and
- c) solidifying the aluminum-zinc alloy, said aluminide particles providing improved spangle facet size reduction of about 0.5 mm and smaller.
In a method of coating a steel product using a molten aluminum-zinc alloy bath having an aluminum content between about 25% and 70% aluminum by weight, the improvement comprising modifying the composition of the aluminum-zinc alloy by:
- a) selecting a particulate compound constituent having a particle size between about 0.01 microns and about 25 microns, said particulate compound constituent selected from the group consisting of a carbide compound containing titanium, a carbide compound containing vanadium, a carbide compound containing iron, and a carbide compound containing tungsten;
- b) adding an effective amount of at least one selected carbide compound to the bath;
- f) applying the molten aluminum-zinc alloy along with said carbide particles to the steel product;
- and
- c) solidifying the aluminum-zinc coating, said carbide particles providing a facet size of about 0.5 mm and smaller.