Aluminum base alloy containing boron and manufacturing method thereof

Abstract

A aluminum base alloy containing boron and manufacturing method thereof, said alloy exhibiting good mechanical properties (such as high-temperature strength and creep strength) over a long period of time and also having a neutron absorbing capacity owing to boron present therein in the form of a compound without segregation. The alloy contains 0.5–10 mass % of boron with an isotopic element satisfying a relation of 10B/(10B +11B)≦30%. said boron being present in the form of a boron compound which is 300 μm or below in size. The alloy is obtained by melting at a temperature in excess of 950° C. and cast at a temperature in the range of 800° C. to 950° C., in such a way that the molten metal is kept for 60–180° seconds until it cools from 950° C. to the casting temperature.