US 7,118,461 B2Granted
Smooth pads for CMP and polishing substrates
AssigneeThomas West, Inc.
InventorsThomas E. West, Guangwei Wu, Donald P. Dietz
Life of this patent
Estimating the term…
Abstract
Pads and methods of making the pads for applications such as polishing substrates and chemical mechanical planarization of substrates are provided. The pads include a substantially smooth surface for improved performance.
Claims8
A method of making a pad for chemical mechanical planarization of a substrate, the method comprising the steps of:
- providing a composite of non-woven felt of polymer fibers impregnated with a resin;
- and
- generating a smooth surface on the composite so that the smooth surface has a surface finish substantially equal to a surface finish that results from polishing the composite with an abrasive having particle grit sizes greater than 300, wherein the step of generating the smooth surface comprises removing about 50 micrometers from the surface of the composite using abrasive particles having an average size of about 30 micrometers followed by removing about 50 micrometers from the surface of the composite using abrasive particles having an average size of about 15 micrometers.
A method of making a pad, the pad having a density of about 0.5 grams per cubic centimeter to about 0.7 grams per cubic centimeter, the method comprising the steps of:
- providing a non-woven felt of polymer fibers, the felt having a density greater than about 0.29 grams per cubic centimeter;
- providing a resin;
- impregnating the felt with the resin so as to form a composite of felt and resin wherein the ratio of weight percent fiber to weight percent resin is in the range from about 35:65 to about 65:35;
- and generating a smooth surface on the composite so that the smooth surface has a surface finish substantially equal to the surface finish produced by polishing the composite with abrasive particles less than 50 micrometers in size.