Polymer additive compositions comprising highly versatile thermoplastic nucleators

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent induces a crystallization cycle time (t1/2) of at most 2.0 minutes in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation, at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation comprising said nucleating agent is extruded then molded into plaques having dimensions of about 61 mm×76 mm×1.27 mm, wherein said t1/2 cycle time is measured by differential scanning calorimetry at a constant crystallization temperature of about 140° C., and wherein said nucleator also exhibits no appreciable fugitivity from said polypropylene formulation during compounding of said test homopolymer polypropylene formulation comprising said nucleating agent, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one acid scavenger and optionally comprises at least one thermoplastic polymer and at least one compound selected from the group consisting of plasticizers, antioxidants, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent induces a standard peak crystallization temperature of at least 123.5° C. in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation comprising said nucleating agent is extruded then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, wherein said peak crystallization temperature measured by differential scanning calonmetry in accordance with a modified ASTM Test Method D3417-99 at heating and cooling rates of 20° C./minute, wherein said nucleator is present in at most 1500 ppm, wherein said nucleator agent exhibits no appreciable fugitivity from said polypropylene formulation during compounding of said polypropylene formulation with said nucleating agent, and wherein said nucleating agent further induces said peak crystallization temperature within said polypropylene formulation when no calcium stearate is present therein, and
• wherein said nucleating agent provides a comparative peak crystallization temperature of at most 2° C. lower than said standard peak crystallization for the same polypropylene formulation when at least 800 ppm of calcium stearate is present therein, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one acid scavenger and optionally comprises at least one thermoplastic polymer and at least one compound selected from the group consisting of plasticizers, antioxidants, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent produces an effective nucleation density of greater than 7×109 nuclei/cm3 at an isothermal crystallization temperature of about 148° C. in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation is extruded then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, and wherein said nucleating agent also exhibits no appreciable fugitivity from said test homopolymer polypropylene formulation during compounding of said test homopolymer polypropylene formulation comprising said nucleating agent,
• wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one acid scavenger and optionally comprises at least one thermoplastic polymer and at least one compound selected from the group consisting of plasticizers, antioxidants, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent exhibits a nucleation effectiveness factor (NEF) of greater than 0.06 in a test homopolymer polypropylene formulation having a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C.,
• wherein said formulation is extruded and then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one acid scavenger and optionally comprises at least one thermoplastic polymer and at least one compound selected from the group consisting of plasticizers, antioxidants, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent induces a peak crystallization temperature of at least 125° C. for a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation comprising said nucleating agent is extruded then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, wherein said peak crystallization temperature is measured by differential scanning calorimetry in accordance with a modified ASTM Test Method D3417-99 at heating and cooling rates of 20° C./minute, and wherein said nucleating agent also exhibits no appreciable fugitivity from said test homopolymer polypropylene formulation during compounding of said test homopolymer polypropylene formulation comprising said nucleating agent, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one thermoplastic polymer and optionally at least one compound selected from the group consisting of plasticizers, antioxidants, acid scavengers, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent induces a crystallization cycle time (t1/2) of at most 2.0 minutes in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min. a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation comprising said nucleating agent is extruded then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, wherein said t1/2 cycle time is measured by differential scanning calorimetry at a constant crystallization temperature of about 140° C., and wherein said nucleator also exhibits no appreciable fugitivity from said polypropylene formulation during compounding of said test homopolymer polypropylene formulation comprising said nucleating agent, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one thermoplastic polymer and optionally at least one compound selected from the group consisting of plasticizers, antioxidants, acid scavengers, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent induces a standard peak crystallization temperature of at least 123.5° C. in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C., and wherein said formulation comprising said nucleating agent is extruded then molded into plaques having dimensions of about 51 mm×76mm×1.27 mm, wherein said peak crystallization temperature measured by differential scanning calorimetry in accordance with a modified ASTM Test Method D3417-99 at heating and cooling rates of 20° C./minute, wherein said nucleator is present in at most 1500 ppm, wherein said nucleator agent exhibits no appreciable fugitivity from said polypropylene formulation during compounding of said polypropylene formulation with said nucleating agent, and wherein said nucleating agent further induces said peak crystallization temperature within said polypropylene formulation when no calcium stearate is present therein, and
• wherein said nucleating agent provides a comparative peak crystallization temperature of at most 2° C. lower than said standard peak crystallization for the same polypropylene formulation when at least 800 ppm of calcium stearate is present therein, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one thermoplastic polymer and optionally at least one compound selected from the group consisting of plasticizers, antioxidants, acid scavengers, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent produces an effective nucleation density of greater than 7×109 nuclei/cm3 at an isothermal crystallization temperature of about 148° C. in a test homopolymer polypropylene formulation comprising said nucleating agent, wherein the unnucleated test homopolymer polypropylene exhibits a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature at 0.46 mPa of about 93° C. and wherein said formulation is extruded then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, and
• wherein said nucleating agent also exhibits no appreciable fugitivity from said test homopolymer polypropylene formulation during compounding of said test homopolymer polypropylene formulation comprising said nucleating agent,
• wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one thermoplastic polymer and optionally at least one compound selected from the group consisting of plasticizers, antioxidants, acid scavengers, antimicrobials, flame retarda, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.

A polymer additive composition comprising a nucleating agent which conforms with the structure of Formula (I)

• wherein M1 and M2 are the same or different, or M1 and M2 are combined to form a single moiety, and are independently selected from the group consisting of metal or organic cations, and R1, R2, R3, R4, R5, R6, R7, R8, R9, and R10 are individually selected from the group consisting of hydrogen, C1–C9 alkyl, hydroxyl, C1–C9 alkoxy, C1–C9 alkyleneoxy, amine, and C1–C9 alkylamine, halogen, phenyl, alkylphenyl, and geminal or vicinal carbocyclic having up to 9 carbon atoms;
• wherein said nucleating agent exhibits a nucleation effectiveness factor (NEF) of greater than 0.06 in a test homopolymer polypropylene formulation having a density of about 0.9 g/cc, a melt flow of about 12 g/10 min, a Rockwell Hardness (R scale) of about 90, a tensile strength of about 4,931 psi, an elongation at yield of about 10%, a flexural modulus of about 203 ksi, an Izod impact strength of about 0.67 ft-lb/in, and a deflection temperature of at 0.46 mPa of about 93° C., wherein said formulation is extruded and then molded into plaques having dimensions of about 51 mm×76 mm×1.27 mm, wherein said additive composition is present in a form selected from the group consisting of a powder, a pellet, and a liquid, and wherein said composition also comprises at least one thermoplastic polymer and optionally at least one compound selected from the group consisting of plasticizers, antioxidants, acid scavenger, antimicrobials, flame retardants, light stabilizers, antistatic agents, blowing agents, colored pigments, and any combination thereof.