Single-step simple and economical process for the preparation of nanosized acicular magnetic iron oxide particles of maghemite phase

A process for the preparation of nanosized acicular magnetic iron oxide particles of maghemite phase of size ranging between 300–350 nm in magnetic field at room temperature by biomimetic route, said process comprising steps of:

• a) mixing polyvinyl alcohol solution of strength ranging between 0.1 to 0.6% and iron salt solution of strength ranging between 0.1–0.15% in a volumetric ratio ranging between 3.1 to 5:2 at a pH in the range of 2–5 and stirring for about 20 minutes by a magnetic stirrer,
• b) heating the resultant solution at a temperature in the range of 30°–60° C. for about 24 hours in an oven under nitrogen atmosphere to obtain an iron ion loaded polymer gel,
• c) soaking the above said polymer gel for a period ranging from 4–6 minutes into sodium hydroxide solution of strength ranging between 2–2.5 M at a temperature ranging from 30° C.–50° C. under an external magnetic field ranging between 800–1500 Gauss,
• d) washing the above soaked polymer gel with deionized water to remove the sodium chloride salt and drying at a temperature ranging between 30° C.–60° C. under nitrogen atmosphere for about 24 hours, and
• e) recovering the 100% acicular maghemite particles from the dried polymer gel.