Production method for porous metal body
OwnerHideo Nakajimainventor
Life of this patent
Estimating the term…
Abstract
A process for producing a metal body comprises (1) a step of maintaining under reduced pressure a metal material within a temperature range of room temperature to a temperature lower than a melting point of the metal in a sealed vessel to thereby degas the metal material, (2) a step of melting the metal material under pressurization by introducing a gas into the sealed container to thereby dissolve the gas into the molten metal, and (3) a step of cooling and solidifying the molten metal while controlling a gas pressure and a molten metal temperature in the sealed vessel to thereby form a porous metal body.
Claims14
A process for producing a porous metal body, comprising:
- (1) maintaining under reduced pressure in the range between 10−1 and 10−6 Torr a raw metal material within a temperature range which is 50 to 200° C. lower than the melting point of the metal in a sealed vessel to thereby degas the raw metal material;
- (2) melting the raw metal material under pressurization of between 0.1 and 10 MPa by introducing a gas containing nitrogen gas and one or more gases selected from the group consisting of hydrogen, argon, and helium into the sealed vessel to thereby dissolve the gas in the molten metal;
- and
- (3) pouring the molten metal into a mold equipped with a cooling apparatus while controlling the gas pressure above and the temperature of the molten metal, cooling and solidifying the molten metal in the mold inside the sealed vessel to form a porous metal body.
A method for producing a porous metal comprising:
- holding a metal under a pressure of between 101 and 106 Torr and at a temperature lower by 50 to 200° C. than the melting point of the metal in a sealed vessel, thereby degassing the metal;
- melting the metal under a pressure of between 0.1 and 10 MPa while introducing a gas mixture containing nitrogen gas and at least one gas selected from the group consisting of hydrogen, argon, and helium into the sealed vessel, thereby dissolving a part of the gas in the molten metal;
- and
- pouring the molten metal into a mold, and cooling and solidifying the molten metal in the mold to produce a porous metal.
A process for producing a porous metal body, comprising:
- (1) maintaining under reduced pressure in the range between 10−1 and 10−6 Torr a raw metal material within a temperature range which is 50 to 200° C. lower than the melting point of the metal in a sealed vessel to thereby degas the raw metal material;
- (2) melting the raw metal material under pressurization of between 0.1 and 10 MPa by introducing a gas containing a nitrogen-argon mixture, a nitrogen-helium mixture or a nitrogen-argon-helium mixture into the sealed vessel to thereby dissolve the gas in the molten metal;
- and
- (3) pouring the molten metal into a mold equipped with a cooling apparatus while controlling the gas pressure above and the temperature of the molten metal, cooling and solidifying the molten metal in the mold inside the sealed vessel to form a porous metal body.
A method for producing a porous metal comprising:
- holding a metal under a pressure of between 10−1 and 10−6 Torr and at a temperature lower by 50 to 200° C. than the melting point of the metal in a sealed vessel, thereby degassing the metal;
- melting the metal under a pressure of between 0.1 and 10 MPa while introducing a nitrogen-argon mixture, a nitrogen-helium mixture or a nitrogen-argon-helium mixture into the sealed vessel, thereby dissolving a part of the gas in the molten metal;
- and
- pouring the molten metal into a mold, and cooling and solidifying the molten metal in the mold to produce a porous metal.
A process for producing a porous metal body, comprising:
- (1) maintaining under reduced pressure in the range between 10−1 and 10−6 Torr a raw metal material within a temperature range which is 50 to 200° C. lower than the melting point of the metal in a sealed vessel to thereby degas the raw metal material;
- (2) melting the raw metal material under pressurization of between 0.1 and 10 MPa by introducing a nitrogen gas into the sealed vessel to thereby dissolve the gas in the molten metal;
- and
- (3) pouring the molten metal into a mold equipped with a cooling apparatus while controlling the gas pressure above and the temperature of the molten metal, cooling and solidifying the molten metal in the mold inside the sealed vessel to form a porous metal body.
Dependencies are inferred from the claim text.