Process for preparing polymer latex resin powder
AssigneeLC Chem, Ltd.
InventorsJi-Hyun Lee, Byung-Tae Yang, Chan-Hong Lee
Life of this patent
Estimating the term…
Abstract
The present invention relates to a process for preparing polymer latex resin powder, and particularly to a process for preparing polymer latex resin powder including coagulating polymer latex and aging the polymer latex. The process further includes introducing an emulsifier into polymer latex emulsion before coagulation. The polymer latex resin powder prepared by the present invention has 85 wt % or more of particles with diameter of 70 to 400 μm, each 10 wt % or less of fine powder with less than 70 μm and those with 400 μm or more, and it has superior bulk density and caking property.
Claims6
A process for preparing polymer latex resin powder comprising;
- introducing an emulsifier into a storage tank containing a polymer latex emulsion to form a polymer latex;
- continuously supplying the polymer latex, primary coagulant and water to a primary coagulation tank to prepare a mixture, wherein the primary coagulant is diluted to concentration of 5 to 10 wt % with water and introduced in an amount of 0.5 to 2.5 weight parts per 100 weight parts of polymer;
- primary coagulating the mixture in the primary coagulation tank by allowing the mixture to remain for 2 to 5 minutes to prepare a primary coagulated slurry wherein a temperature of the primary coagulation tank is 30 to 40° C. lower than or equal to the glass transition temperature of the polymer latex and transferring the prepared primary coagulated slurry to a secondary coagulation tank;
- secondary coagulating in the primary coagulated slurry in the secondary coagulation tank by allowing the primary coagulated slurry to remain for 10 to 25 minutes to prepare a secondary coagulated slurry wherein a temperature of the secondary coagulation tank is 1 to 10° C. greater than or equal to the temperature of the primary coagulation tank, and transferring the prepared secondary coagulated slurry to a primary aging tank, wherein the secondary coagulant is introduced in an amount of 2 to 3 weight parts per 100 weight parts of polymer;
- primary aging the secondary coagulated slurry in the primary aging tank by allowing the secondary coagulated slurry to remain for 60 to 90 minutes to prepare a primary aged slurry, wherein a temperature of the primary aging tank is 5 to 20° C. greater than or equal to the temperature of the secondary coagulation tank, and transferring the prepared primary aged slurry to a secondary aging tank;
- and
- secondary aging the primary aged slurry in the secondary aging tank by allowing the primary aged slurry to remain for 60 to 90 minutes, wherein a temperature of the secondary aging tank is 10 to 20° C. greater than or equal to the temperature of the primary aging tank.