Truck tire with cap/base construction tread
AssigneeThe Goodyear Tire & Rubber Company
InventorsFahri Özel, Michel Pierre Charles Robert
Life of this patent
Estimating the term…
Abstract
A pneumatic tire comprising a tread, the tread comprising a tread cap and a tread base in a tread base to tread cap volume ratio ranging from about 0.25 to about 1; the tread cap comprising, based on 100 parts by weight rubber (phr): 100 phr of cis 1,4 polyisoprene natural rubber; from about 25 to about 50 phr of carbon black; and from about 8 to about 35 phr of silica; the tread base comprising, based on 100 parts by weight rubber (phr): 100 phr of cis 1,4 polyisoprene natural rubber; from about 25 to about 50 phr of carbon black; and from about 8 to about 35 phr of silica; wherein the tread cap has a stiffness greater than that of the tread base.
Claims6
A pneumatic tire comprising a tread, said tread comprising a tread cap and a tread base;
- said tread cap comprising, based on 100 parts by weight rubber (phr):
- 100 phr of cis 1,4 polyisoprene natural rubber;
- from about 25 to about 45 phr of carbon black;
- and from about 8 to about 35 phr of silica;
- said tread base comprising, based on 100 parts by weight rubber (phr):
- 100 phr of cis 1,4 polyisoprene natural rubber;
- from about 25 to about 50 phr of carbon black;
- and from about 8 to about 35 phr of silica;
- wherein said tread cap has a stiffness greater than that of said tread base, said stiffness characterized by a 300 percent modulus, said tread cap having a 300 percent modulus ranging from about 10 MPa to about 12 MPa and said tread base having a 300 percent modulus ranging from about 8 MPa to about 11 MPa;
- said tread comprising a tread base to tread cap volume ratio ranging from about 0.5 to about 1.
A pneumatic tire comprising a tread, said tread comprising a tread cap and a tread base;
- said tread cap comprising, based on 100 parts by weight rubber (phr):
- 100 phr of cis 1,4 polyisoprene natural rubber;
- from about 25 to about 45 phr of carbon black;
- and from about 8 to about 35 phr of silica;
- said tread base comprising, based on 100 parts by weight rubber (phr):
- 100 phr of cis 1,4polyisoprene natural rubber;
- from about 25 to about 50 phr of carbon black;
- and from about 8 to about 35 phr of silica;
- wherein said tread cap has a stiffness greater than that of said tread base, said stiffness characterized by a modulus G′, said tread cap having G′ ranging from about 1.2 MPa to about 1.6 MPa and said tread base having G′ ranging from about 1.0 MPa to about 1.3 MPa;
- said stiffness further characterized by a 300 percent modulus, said tread cap having a 300 percent modulus ranging from about 10 MPa to about 12 MPa and said tread base having a 300 percent modulus ranging from about 8 MPa to about 11 MPa;
- said tread comprising a tread base to tread cap volume ratio ranging from about 0.5 to about 1.