Method for controlling a direction of polarization of a piezoelectric thin film
AssigneeMatsushita Electric Industrial Co., Ltd.
InventorsSatoru Fujii, Isaku Kanno, Ryoichi Takayama, Takeshi Kamada
Life of this patent
Estimating the term…
Abstract
To manufacture a compact and high-performance thin-film piezoelectric bimorph element at low cost, first and second piezoelectric thin films (2, 3) are formed by sputtering on the both surfaces of a metal thin plate (1) which are opposing relation to each other along the thickness thereof, while the respective states of polarizations of the first and second piezoelectric thin films (2, 3) are controlled. A pair of electrode films (5) are formed on the respective surfaces of the first and second piezoelectric thin films (2, 3) opposite to the metal thin plate (1).
Claims2
A method for controlling a direction of polarization of a piezoelectric thin film during the forming of the piezoelectric thin film by sputtering on one surface of a metal thin plate, the method comprising the steps of:
- forming the piezoelectric thin film by sputtering on one surface of the metal thin plate, while controlling a temperature of the metal thin plate such that a direction of a pyroelectric current of the piezoelectric thin film flows from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate, when the direction of polarization of the piezoelectric thin film is to be set from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate;
- and
- forming the piezoelectric thin film by sputtering on one surface of the metal thin plate, while controlling a temperature of the metal thin plate such that a direction of the pyroelectric current of the piezoelectric thin film flows from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate, when the direction of polarization of the piezoelectric thin film is to be set from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate,
- wherein the piezoelectric thin film is PbpLaqTirZrsO3,
- wherein when the direction of polarization of the piezoelectric thin film is set from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate;
- the temperature of the metal thin plate is set between a range of 500° C. and 630° C., and
- wherein when the direction of polarization of the piezoelectric thin film is set from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate, the temperature of the metal thin plate is set between a range of 670° C. and 750° C.
A method for controlling a direction of polarization of a piezoelectric thin film during the forming of the piezoelectric thin film by sputtering on one surface of a metal thin plate, the method comprising the steps of:
- forming the piezoelectric thin film by sputtering on one surface of the metal thin plate, while controlling a temperature of the metal thin plate such that a direction of a pyroelectric current of the piezoelectric thin film flows from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate, when the direction of polarization of the piezoelectric thin film is to be set from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate;
- and
- forming the piezoelectric thin film by sputtering on one surface of the metal thin plate, while controlling a temperature of the metal thin plate such that a direction of the pyroelectric current of the piezoelectric thin film flows from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate, when the direction of polarization of the piezoelectric thin film is to be set from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate,
- wherein the piezoelectric thin film is PbpLaqTirZrsO3,
- wherein when the direction of polarization of the piezoelectric thin film is set from the side of the metal thin plate of the piezoelectric thin film to the side opposite to the metal thin plate, the temperature of the metal thin plate is set between a range of 570° C. and 630° C., and
- wherein when the direction of polarization of the piezoelectric thin film is set from the side opposite to the metal thin plate of the piezoelectric thin film to the side of the metal thin plate, the temperature of the metal thin plate is set between a range of 670° C. and 720° C.
Dependencies are inferred from the claim text.