Ni hydrogenation catalysts, manufacture and use
AssigneeCatalytic Distillation Technologies
InventorsJ. Yong Ryu, Hugh M. Putman
Life of this patent
Estimating the term…
Abstract
Improved Ni catalysts for hydrogenation reactions are disclosed. The catalysts are useful for hydrogenation such as selective hydrogenation of acetylenic impurities in crude olefin and diolefin streams. The catalysts are prepared by depositing nickel on a porous support which has the following specific physical properties; BET surface area of from 30 to about 100 m2/g, total nitrogen pore volume of from 0.4 to about 0.9 cc/g, and an average pore diameter of from about 110 to 450 Å with or without modifiers of one or more elements selected from the group consisting of Cu, Re, Pd, Zn, Mg, Mo, Ca and Bi.
Claims4
A catalyst useful for the selective hydrogenation of acetylenic impurities in crude olefin and diolefin streams consisting of about 9.67 to about 20 wt. % Ni and one or more elements selected from the group consisting of from about 0.005 wt. % to about 10 wt. % Cu, from about 0.1 to about 10 wt. % Zn, from about 0.1 to about 7 wt. % Mg, from about 0.1 to about 7 wt. % Ca and from about 0.05 to about 7 wt. % Bi deposited on an alumina support having the following physical properties:
- BET surface area of from 30 to about 100 m2/g, total nitrogen pore volume of from 0.4 to about 0.9 cc/g, and an average pore diameter of from about 110 to 450, at least 50% of the pores larger than 100 Å diameter, and a total pore volume from about 0.405 cc/g to about 0.9 cc/g and ABD (apparent bulk density) from about 0.35 to about 0.75 g/cc Å.
A selective hydrogenation catalyst comprising from about 4 wt. % to about 20 wt. % Ni and from about 0.05 to about 7 wt. % Bi deposited on a support having the following physical properties:
- BET surface area of from 30 to about 100 m2/g, total nitrogen pore volume of from 0.4 to about 0.9 cc/g, and an average pore diameter of from about 110 to 450 Å.
Dependencies are inferred from the claim text.