US 7,022,280 B2Granted
Process of making a flat yarn from polyoxymethylene film
AssigneePolyplastics Co., Ltd.
InventorHidetoshi Okawa
Life of this patent
Estimating the term…
Abstract
A flat yarn of a high strength and a high modulus of elasticity, being excellent in solvent resistance, thermal stability and resistance to bending fatigue is provided. The flat yarn comprises polyoxymethylene copolymer containing 0.5 to 10 moles of specified oxyalkylene units per 100 moles of oxymethylene units in the polymer chain principally comprising repeating oxymethylene units and having a melt index at 190° C. with load of 2160 g of 0.3 to 20 g/10 min.
Claims14
A process for producing a flat yarn, which comprises the steps of:
- (a) providing a polyoxymethylene copolymer having a melt index at 190° C. with a load of 2160 g of 0.3 to 20 g/10 min., the polyoxymethylene copolymer being comprised mainly of repeating oxymethylene units and containing 0.5 to 10 moles of oxyalkylene units represented by the following formula (1) per 100 moles of the oxymethylene units in the polymer chain:
- in which R1 and R2 represent hydrogen atom, an alkyl group of 1 to 8 carbon atoms, an organic group having an alkyl group of 1 to 8 carbon atoms, a phenyl group or an organic group having a phenyl group, R1 and R2 may be identical to or different from each other and m represents an integer of 2 to 6;
- (b) melting the polyoxymethylene copolymer provided according to step (a) and forming a film therefrom by inflation extrusion or T-die extrusion;
- (c) slitting the film obtained according to step (b) into a plurality of strips by passing the film through a slitter;
- (d) monoaxially stretching the strips obtained in step (c) 2 to 15 times at a temperature of between 80° C. and 170° C.;
- and then
- (e) heat-setting the monoaxially stretched strips at a temperature between 120° C. and 180° C. to obtain a flat yarn thereof.
4 more elements
A process for producing a flat yarn, which comprises the steps of:
- (a) providing a polyoxymethylene copolymer having a melt index at 190° C. with a load of 2160 g of 0.3 to 20 g/10 min., the polyoxymethylene copolymer being comprised mainly of repeating oxymethylene units and containing 0.5 to 10 moles of oxyalkylene units represented by the following formula (1) per 100 moles of the oxymethylene units in the polymer chain:
- in which R1 and R2 represent hydrogen atom, an alkyl group of 1 to 8 carbon atoms, an organic group having an alkyl group of 1 to 8 carbon atoms, a phenyl group or an organic group having a phenyl group, R1 and R2 may be identical to or different from each other and m represents an integer of 2 to 6;
- (b) melting the polyoxymethylene copolymer provided according to step (a) and forming a film therefrom by inflation extrusion or T-die extrusion;
- (c) slitting the film obtained according to step (b) into a plurality of strips by passing the film through a slitter;
- (d) monoaxially stretching the strips obtained in step (c) 2 to 15 times at a temperature which is between the glass transition point and the melting point of the polyoxymethylene copolymer;
- and then
- (e) heat-setting the monoaxially stretched strips at a temperature between 120° C. and the melting point of the polyoxymethylene copolymer to obtain a flat yarn thereof.
4 more elements
Dependencies are inferred from the claim text.