Back to results
US 7,008,895 B2Granted
Method for producing an improved supported catalyst
OwnerDavid Deck Rendinainventor
Life of this patent
Estimating the term…
Abstract
Highly active supported catalyst compositions and methods for producing more active supported catalyst compositions are disclosed. Said methods comprise steps for applying an adhesive coating of a catalytically active exfoliated transition metal dichalcogenide and promoters to the surface of a support medium prior to filling the pores of the support medium with catalytically active metals and/or promoters. A new method for applying a surface coating to a support is also disclosed.
Claims17
A catalytically active composition of matter of the following approximate general formula:
- P1:M1-S-M2:P2
- Where:
- P1 is selected from athe group of materials that promote catalytic activity and that form as an inclusion within sheets of an exfoliated transition metal dichalcogenide comprising 0–15 percent by weight of the final composition,
- M1:
- is selected from athe group of catalytically active exfoliated transition metal dichalcogenides comprised of group IVB, VB, VIB elements that can be deposited as sheets on the surface of a support material, comprising 1–90 percent by weight of the final composition,
- S:
- is selected from athe group of porous, largely inert support materials to which exfoliated transition metal dichalcogenides will adhere, comprising 10–90 percent by weight of the final catalyst composition,
- M2:
- is selected from athe group of catalytically active materials that can be formed from precursors within the pores of said support material, comprising 1–30 percent by weight of the final catalyst composition,
- P2:
- is selected from athe group of materials that promote catalytic activity and that can be formed from precursors within the pores of said support material comprising 0–15 percent by weight of the final catalyst composition, in which the support material is comprised of naturally occurring minerals.
8 more elements
A catalytically active composition of matter of the following approximate general formula:
- P1:M1-S-M2:P2
- Where:
- P1 is selected from athe group of materials that promote catalytic activity and that form as an inclusion within sheets of an exfoliated transition metal dichalcogenide, comprising 0–15 percent by weight of the final composition,
- M1:
- is selected from athe group of catalytically active exfoliated transition metal dichalcogenides comprised of group IVB, VB, VIB elements that can be deposited as sheets on the surface of a support material, comprising 1–90 percent by weight of the final composition,
- S:
- is selected from athe group of porous, largely inert support materials to which exfoliated transition metal dichalcogenides will adhere, comprising 10–90 percent by weight of the final catalyst composition.
- M2:
- is selected from athe group of catalytically active materials that can be formed from precursors within the pores of said support material, comprising 1–30 percent by weight of the final catalyst composition,
- P2:
- is selected from athe group of materials that promote catalytic activity and that can be formed from precursors within the pores of said support material comprising 0–15 percent by weight of the final catalyst composition, in which the support material is comprised of carbon.
8 more elements
A catalytically active composition of matter of the following approximate general formula:
- P1:M1-S-M2:P2
- Where:
- P1 is selected from athe group of materials that promote catalytic activity and that form as an inclusion within sheets of an exfoliated transition metal dichalcogenide, comprising 0–15 percent by weight of the final composition,
- M1:
- is selected from athe group of catalytically active exfoliated transition metal dichalcogenides comprised of group IVB, VB, VIB elements that can be deposited as sheets on the surface of a support material, comprising 1–90 percent by weight of the final composition,
- S:
- is selected from athe group of porous, largely inert support materials to which exfoliated transition metal dichalcogenides will adhere, comprising 10–90 percent by weight of the final catalyst composition,
- M2:
- is selected from athe group of catalytically active materials that can be formed from precursors within the pores of said support material, comprising 1–30 percent by weight of the final catalyst composition,
- P2:
- is selected from athe group of materials that promote catalytic activity and that can be formed from precursors within the pores of said support material comprising 0–15 percent by weight of the final catalyst composition, in which the support material is synthesized, in which the support material is comprised of synthetic zeolite.
8 more elements
A process for the preparation of a catalytically active composition of matter of the following approximate general formula:
- P1:M1-S-M2:P2
- Where:
- P1 is selected from athe group of materials that promote catalytic activity and that form as an inclusion within sheets of an exfoliated transition metal dichalcogenide, comprising 0–15 percent by weight of the final composition,
- M1:
- is selected from athe group of catalytically active exfoliated transition metal dichalcogenides comprised of group IVB, VB, VIB elements that can be deposited as sheets on the surface of a support material, comprising 1–90 percent by weight of the final composition,
- S:
- is selected from athe group of porous, largely inert support materials to which exfoliated transition metal dichalcogenides will adhere, comprising 10–90 percent by weight of the final catalyst composition,
- M2:
- is selected from athe group of catalytically active materials that can be formed from precursors within the pores of said support material, comprising 1–30 percent by weight of the final catalyst composition,
- P2:
- is selected from athe group of materials that promote catalytic activity and that can be formed from precursors within the pores of said support material comprising 0–15 percent by weight of the final catalyst composition, the process comprising the following steps:
- a) coating a selected catalyst support material (S) wit active catalytic materials in the form of exfoliated sheets of transition metal dichalcogenides, preferably exfoliated sheets of molybdenum and/or tungsten metal sulfides (M1), with or without inclusions of promoter materials (P1),
- b) drying the coating in a manner that forms an adhesive bond between the coating and the surface of the support,
- c) filling the pores of the support with additional materials (M2) and optionally materials (P2).
11 more elements
A method for forming an exfoliated transition metal coated support material said method comprising the following steps:
- a) including a support precursor between sheets of the exfoliated material
- b) heating the combined materials in a manner, and in an atmosphere, that converts the precursor to the desired support material without chemically altering the exfoliated transition metal dichalcogenide.
Dependencies are inferred from the claim text.