US 6,991,022 B2Granted
Investment casting mold and method of manufacture
AssigneeBuntrock Industries, Inc.
InventorsJohn Vandermeer, Kermit A. Buntrock, Thomas M. Branscomb, Arlen G. Davis
Life of this patent
Estimating the term…
Abstract
The invention relates to investment casting shell molds and their method of manufacture. The method entails mixing fiber such as ceramic refractory fiber and organic fiber with ceramic filler to form a dry blend. The dry blend is mixed with a binder sol such as colloidal silica sol to form slurry. An expendable preform is dipped into the slurry, stuccoed and dried. This step is repeated until a ceramic shell of a desired thickness is formed over the expendable preform. The expendable preform then is removed, and the green ceramic shell is fired. Molten metal then may be poured into the shell to form a metal casting.
Claims36
A method of manufacture of an investment casting mold comprising,
- mixing one or more fibers selected from the group consisting of organic fiber, ceramic fiber and mixtures thereof with one or more ceramic fillers to form a first dry blend,
- mixing fiber and ceramic filler to form a second dry blend which is the same or different from the first dry blend,
- mixing the first dry blend with a first colloidal sol to form prime coat slurry,
- mixing the second dry blend with a second colloidal sol to form a backup coat slurry wherein the second colloidal silica sol is the same or different from the first colloidal silica sol and wherein the backup coat slurry is the same or different from the prime coat slurry,
- applying a coating of the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform,
- drying the stuccoed, prime coated preform,
- applying a coating of the backup coat slurry onto the stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
9 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with a first colloidal silica sol to produce a first prime coat slurry,
- mixing ceramic filler with organic fiber to form a dry blend wherein the ceramic filler is the same or different from any one of the ceramic fillers in the first prime coat slurry,
- mixing the dry blend with a second colloidal silica sol to form a second prime coat slurry wherein the second colloidal silica sol is the same or different from the first colloidal sol,
- mixing the dry blend with a third colloidal silica sol to produce a backup coat slurry wherein the third colloidal silica sol is the same or different from each of the first colloidal sol and the second colloidal sol,
- applying the first prime coat slurry onto an expendable preform to produce a first prime coated preform,
- applying a stucco onto the first prime coated preform to produce a stuccoed, first prime coated preform,
- drying the stuccoed, first prime coated preform to produce a dried, stuccoed first prime coated preform,
- applying the second prime coat slurry onto the dried, stuccoed first prime coated preform to produce a preform having a plurality of prime coats,
- applying stucco to the preform having a plurality of prime coats to produce a stuccoed preform having a plurality of prime coats,
- drying the stuccoed preform to produce a dried, stuccoed preform having a plurality of prime coats,
- applying the backup coat slurry to the dried, stuccoed preform having a plurality of prime coats to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
12 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with a first colloidal silica sol to produce a first prime coat slurry,
- mixing a ceramic filler with ceramic fiber to produce a dry blend wherein the ceramic filler is the same or different from any of the ceramic fillers in the first prime coat slurry,
- mixing the dry blend with a second colloidal silica sol to form a backup coat slurry wherein the second colloidal silica sol is the same or different from the first colloidal sol,
- applying the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the backup coat slurry to the dried, stuccoed prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
8 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with a first colloidal silica sol to produce a first prime coat slurry,
- mixing fused silica and polypropylene fiber to form a dry blend,
- mixing the dry blend with a second colloidal silica sol to form a second prime coat slurry wherein the second colloidal silica sol is the same or different from the first colloidal silica sol,
- mixing the dry blend with a third colloidal silica sol to produce a backup coat slurry wherein the third colloidal silica sol is the same or different from each of the first colloidal sol and the second colloidal sol,
- applying the first prime coat slurry onto an expendable preform to produce a first prime coated preform,
- applying stucco onto the first prime coated preform to produce a stuccoed, first prime coated preform,
- drying the stuccoed, first prime coated preform to produce a dried, stuccoed first prime coated preform,
- applying the second prime coat slurry onto the dried, stuccoed first prime coated preform to produce a preform having a plurality of prime coats,
- applying stucco to the preform to produce a stuccoed preform having a plurality of prime coats,
- drying the stuccoed preform to produce a dried, stuccoed preform having a plurality of prime coats,
- applying the backup coat slurry to the dried, stuccoed preform having a plurality of prime coats to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
12 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with a first colloidal silica sol to produce a first prime coat slurry,
- mixing organic fiber with a ceramic filler to form a dry blend wherein the ceramic filler is the same or different from any of the ceramic fillers in the first prime coat slurry,
- mixing the dry blend with a second colloidal silica sol to form a second prime coat slurry wherein the second colloidal silica sol is the same or different from the first colloidal sol,
- mixing the dry blend with a third colloidal silica sol to produce a backup coat slurry wherein the third colloidal silica sol is the same or different from each of the first colloidal sol and the second colloidal sol,
- applying the first prime coat slurry onto an expendable preform to produce a first prime coated preform,
- applying stucco onto the first prime coated preform to produce a stuccoed, first prime coated preform,
- drying the stuccoed, first prime coated preform to produce a dried, stuccoed first prime coated preform,
- applying the second prime coat slurry onto the dried, stuccoed first prime coated preform to produce a preform having a plurality of prime coats,
- applying stucco to the preform having a plurality of prime coats to produce a stuccoed preform having a plurality of prime coats,
- drying the stuccoed preform to produce a dried, stuccoed preform having a plurality of prime coats,
- applying the backup coat slurry to the dried, stuccoed preform having a plurality of prime coats to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
12 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with a first aqueous colloidal silica sol to produce a first prime coat slurry,
- mixing nylon fiber with a ceramic filler which is the same or different from any of the ceramic fillers in the first prime coat slurry to form a dry blend,
- mixing the dry blend with a second aqueous colloidal silica sol to form a second prime coat slurry wherein the second aqueous colloidal silica sol is the same or different from the first colloidal sol,
- mixing the dry blend with a third aqueous colloidal silica sol to produce a backup coat slurry wherein the third aqueous colloidal silica sol is the same or different from each of the first colloidal sol and the second colloidal sol,
- applying the first prime coat slurry onto an expendable preform to produce a first prime coated preform,
- applying stucco onto the first prime coated preform to produce a stuccoed, first prime coated preform,
- drying the stuccoed, first prime coated preform to produce a dried, stuccoed first prime coated preform,
- applying the second prime coat slurry onto the dried, stuccoed first prime coated preform to produce a preform having a plurality of prime coats,
- applying stucco to the preform having a plurality of prime coats to produce a stuccoed preform having a plurality of prime coats,
- drying the stuccoed preform to produce a dried, stuccoed preform having a plurality of prime coats,
- applying the backup coat slurry to the dried, stuccoed preform having a plurality of prime coats to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
12 more elements
A method of manufacture of an investment casting mold comprising,
- mixing ceramic filler and ceramic fiber to form a dry blend,
- mixing the dry blend with an aqueous colloidal silica sol to form a prime coat slurry,
- applying the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- mixing ceramic fillers and organic fiber to form a dry blend,
- mixing the blend with an aqueous colloidal silica sol to form a prime coat slurry,
- applying the slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- mixing ceramic filler, ceramic fiber and organic fiber to form a dry blend,
- mixing the blend with an aqueous colloidal silica sol to produce a prime coat slurry,
- applying the slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- forming a dry blend from a mixture of ceramic fillers and ceramic fiber,
- mixing the blend with an aqueous colloidal silica sol to form a prime coat slurry,
- applying the slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- forming a blend from a first mixture of ceramic fillers, and a second mixture of ceramic fibers,
- mixing the blend with an aqueous colloidal silica sol to form a prime coat slurry,
- applying the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- forming a blend from a first mixture of ceramic fillers and a second mixture of ceramic filler and organic fiber,
- mixing the blend with an aqueous colloidal silica sol to form a prime coat slurry,
- applying the slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- forming a blend from a first mixture of ceramic fillers, and a second mixture of ceramic fiber and organic fiber,
- mixing the blend with an aqueous silica sol to produce a prime coat slurry,
- applying the slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the slurry onto the dried, stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with an aqueous colloidal silica sol to produce a prime coat slurry,
- mixing a dry blend of ceramic filler and fiber with an aqueous colloidal silica sol to form a backup coat slurry,
- applying the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the backup coat slurry to the stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
A method of manufacture of an investment casting mold comprising,
- mixing one or more ceramic fillers with an aqueous colloidal silica sol to produce a prime coat slurry that is substantially free of fiber,
- mixing a dry blend of ceramic filler and fiber with an aqueous colloidal silica sol to form a backup coat slurry,
- applying the prime coat slurry onto an expendable preform to produce a prime coated preform,
- applying stucco onto the prime coated preform to produce a stuccoed, first prime coated preform,
- drying the stuccoed, prime coated preform to produce a dried, stuccoed prime coated preform,
- applying the backup coat slurry to the stuccoed, prime coated preform to produce a backup coated preform,
- applying stucco onto the backup coated preform to produce a stuccoed, backup coated preform,
- drying the stuccoed, backup coated preform,
- removing the expendable preform from the backup coated preform to produce a green shell mold, and
- heating the green shell mold to a temperature sufficient to produce a fired ceramic shell mold.
7 more elements
Dependencies are inferred from the claim text.