Vacuum brazing method for aluminum-based material
AssigneeDelphi Technologies, Inc.
InventorsKarl Paul Kroetsch, Ange D. Koeppen, Charles K. Rottner
Life of this patent
Estimating the term…
Abstract
A vacuum brazing method is disclosed for joining aluminum stock materials to each other. The typical cladding material utilized includes aluminum and a melting point lowering agent such as silicon. In addition, the cladding material typically includes magnesium to provide for enhanced wetting of the cladding material into the joint area. It has been found that adjusting the ratio of magnesium to calcium to a level of equal to or greater than 625 to 1 provides greatly enhanced brazed joint formation and reliability of the vacuum brazing method.
Claims20
A method for forming a vacuum brazing cladding material comprising the steps of:
- a) providing a base material of aluminum, an aluminum alloy, or mixtures thereof;
- b) combining the base material with from 0.15 to 0.50% by weight magnesium and from 5 to 15% by weight silicon based on the total weight of the cladding material to form a cladding material;
- and c) adjusting the ratio of magnesium to calcium in the cladding material to a level of at least 625 to 1.
A method for vacuum brazing aluminum stock materials comprising the steps of:
- a) providing two pieces of stock material to be joined, each comprising aluminum, an aluminum alloy, or a mixture thereof;
- b) providing a cladding material comprising a base material of aluminum, an aluminum alloy, or mixtures thereof in combination with from 5 to 15% by weight silicon and 0.15 to 0.5% by weight magnesium based on the total weight of the cladding material, wherein the ratio of magnesium to calcium in the cladding material is at least 625 to 1;
- c) cladding at least a portion of at least one of the pieces of stock material with the cladding material;
- and d) placing the two pieces of stock material adjacent to each other with the cladding material sandwiched between them and vacuum brazing the two pieces of stock material.
A vacuum brazing cladding material comprising a base material of aluminum, aluminum alloy, or mixtures thereof, a melting point lowering agent comprising from 5 to 15% by weight silicon based on the total weight, and from 0.15 to 0.5% by weight magnesium based on total weight, said cladding material having a ratio of magnesium to calcium of at least 625 to 1.
Dependencies are inferred from the claim text.