Material for shadow mask, method for production thereof, shadow mask and image receiving tube
AssigneeToyo Kohan Co., Ltd.
InventorsTaizo Sato, Toshiyuki Ueda, Shinichi Aoki
Life of this patent
Estimating the term…
Abstract
A material for shadow mask having the following composition of components: C≦0.0008 wt %, Si≦0.03 wt %, Mn:0.1 to 0.5 wt %, P≦0.02 wt %, S≦0.02 wt %, Al:0.01 to 0.07 wt %, N≦0.0030 wt %, B: an amount satisfying the formula: 5 ppm≦B−11/14×N≦30 ppm, balance: Fe and inevitable impurities; a method for producing the material; a shadow mask using the material (cold rolled steel sheet); and an image receiving tube equipped with the shadow mask. The material has excellent etching characteristics, which are uniform within the same coil, and excellent press formability.
Claims2
A method for manufacturing shadow mask material made of steel sheet comprising nitrogen equal to or less than 0.0030 wt % and boron (B) satisfying an inequality of 5 ppm≦B−11/14×N≦30 ppm and the residue including iron and unavoidable impurities, wherein said steeel sheet is subjected to hot rolling at a temperature higher than the Ar3 point followed by coiling at a coiling temperature from 540 to 680° C., pickling, cold rolling, and then continuous annealing to control the content ratio of carbon to be no more than 0.0008 wt %.
A method for manufacturing shadow mask material made of steel sheet comprising carbon equal to or less than 0.0008 wt %, silicon equal to or less than 0.03 0.0030 wt %, manganese from 0.1 to 0.5 wt %, phosphorus equal to or less than 0.02 wt. %, sulfur equal to or less than 0.02 wt %, aluminum from 0.01 to 0.07 wt %, nitrogen equal to or less than 0.003 wt % and boron (B) satisfying an inequality of 5 ppm≦B−11/14×N≦30 ppm and the residue including iron and unavoidable impurities, wherein said steel sheet is subjected to hot rolling at a temperature higher than the Ar3 point followed by coiling at a coiling temperature from 540 to 680° C., pickling, cold rolling, and then continuous annealing to control the content ratio of carbon to be no more than 0.0008 wt %.
Dependencies are inferred from the claim text.