Cooling drum for continuously casting thin cast piece and fabricating method and device therefor and thin cast piece and continuous casting method therefor

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine unevenness 1 to 50 μm in average depth and 10 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples adjacent to each other.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples adjacent to each other;
• and also fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples adjacent to each other;
• and fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0,5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples adjacent to each other;
• and fine unevenness 1 to 50 μm in average depth and 10 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples;
• and fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed at the rims and on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine holes 5 μm or more in depth and 5 to 200 m in diameter of circle equivalent are formed at the rims of said dimples;
• and fine unevenness 1 to 50 μm in average depth and 10 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples of a prescribed shape are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine unevenness and fine humps are formed at the rims of said dimples and/or on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 1.0 to 4.0 mm in average diameter and 40 to 200 μm in average depth are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine unevenness 10 to 50 μm in average diameter and 1 to 50 μm in average depth and fine humps 1 to 50 μm in height formed by the intrusion of the fragments of the alumina grit are formed at the rims of said dimples and/or on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples of a prescribed shape are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and the region where the dimples 20 μm or less in average depth exist consecutively at a distance of 1 mm or more accounts for 3% or less.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 1.0 to 4.0 mm in average diameter and 40 to 170 μm in average depth are formed on the peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and the region where the dimples 20 μm or less in average depth exist consecutively at a distance of 1 mm or more accounts for 3% or less.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the plated peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and a film, containing a substance more excellent than Ni in wettability with scum, is formed on said peripheral surface.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the plated peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent are formed on the indented surfaces of said dimples;
• and a film, containing a substance more excellent than Ni in wettability with scum, is formed on said peripheral surface.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the plated peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• and fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent, where a film, containing a substance more excellent than Ni in wettability with scum, is formed, are formed at the rims of said dimples adjacent to each other.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the plated peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine humps 1 to 50 μm in height and 30 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples adjacent to each other;
• and also fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent, where a film, containing a substance more excellent than Ni in wettability with scum, is formed, are formed on the indented surfaces of said dimples.

A cooling drum for metal cast strip by continuous casting, characterized in that:

• dimples 40 to 200 μm in average depth and 0.5 to 3 mm in diameter of circle equivalent are formed on the plated peripheral surface of the cooling drum, adjacent to each other at the rims of said dimples;
• fine holes 5 μm or more in depth and 5 to 200 μm in diameter of circle equivalent are formed at the rims of said dimples;
• and also fine humps 1 to 50 μm in height and 5 to 200 μm in diameter of circle equivalent, where a film, containing a substance more excellent than Ni in wettability with scum, is formed, are formed on the indented surfaces of said dimples.