US 6,887,411 B2Granted
Method for producing polyester blended yarn
AssigneeTeijin Limited
InventorsHiroyuki Osaka, Hideki Beppu, Kenji Iwashita
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeTeijin Limited
InventorsHiroyuki Osaka, Hideki Beppu, Kenji Iwashita
Estimating the term…
A polyester blended yarn giving a woven or knitted fabric exhibiting a swollen touch and a high grade texture is stably obtained by melt-spinning a polyester including A including a substrate polymer including a polyester and 0.5 to 5.0 percent by weight of a polymer P, and the substrate polymer from an identical spinneret or different spinnerets to obtain the filament group A including the polyester composition A and the filament group B including the substrate polymer, blowing cooling air on the filament groups B and A at a speed of 0.20 to 0.80 m/sec and at a speed of not less than 1.1 times said speed, respectively, to once separately cool and solidify the filament groups B and A, doubling the cooled filament groups, and then taking off the obtained doubled yarn at a speed of not less than 2,500 m/min.
A method for producing a polyester blended yarn, characterized by melt-extruding a polyester composition A which comprises a substrate polymer comprising a polyester and 0.5 to 5.0 percent by weight of a polymer P different from the substrate polymer, and the substrate polymer from an identical spinneret or different spinnerets, respectively, to obtain the filament group A comprising the polyester composition A and the filament group B comprising the substrate polymer, once separately cooling and solidifying the filament groups, blowing the cooling air on the filament group B at a speed (BSb) of 0.20 to 0.80 m/sec and the cooling air on the filament group A at a speed (ASb) of not less than 1.1 times the speed (BSb), respectively, doubling the filament groups, and then taking off the obtained blended yarn at a speed of not less than 2,500 m/mm.
A method for producing a polyester blended yarn, characterized by doubling a filament group A obtained by adding a polymer P to a substrate polymer comprising a polyester and then melting, blending and spinning the mixture with a filament group B comprising the substrate polymer and spun from the same spinneret or a different spinneret and then winding up the obtained blended yarn, characterized by disposing a bundling device for bundling the filament group A at the distance GA that is more than GO and not more than 200 cm, wherein GO is a distance between the spinneret face and the necking-starting point of the filament group A, and GA is a distance between the spinneret face for spinning the filament group A and the bundling device.
A method for producing a polyester blended yarn, characterized by once cooling a filament group A obtained by adding a polymethyl methacrylate-based polymer having a melt viscosity MVPM (poise) of not less than 0.6 times a melt viscosity MVPE (poise) of the following polyester and/or a polystyrene-based polymer having a melt viscosity MVPS (poise) of not less than 1.5 times MVPE (poise) in an amount of 0.3 to 5.0 percent by weight based on a substrate polymer comprising the polyester to the substrate polymer, and then blending, melting and spinning the mixture and a filament group B comprising said substrate polymer spun from the same spinneret or a different spinneret at temperatures equal to or lower than the glass transition temperatures, doubling the cooled filament groups A and B, and then winding up the obtained blended yarn.