Reinforcement composition for rotational molding
AssigneeMichael J. Stevenson
InventorsMichael J. Stevenson, Robert Alan Reeves
Life of this patent
Estimating the term…
Abstract
A mixture of a carrier and binder component and polymer powders is provided as a molding composition for sealing rotational molds or for reinforcing selected areas of rotationally molded parts. The carrier and binder component can be very low density polyethylene, petroleum jelly, hydrocarbon wax, hydrocarbon tackifier, or mixtures thereof, and the polymer powders are thermoplastics having a low melt index. The molding composition is applied to selected areas of the rotational mold, such as to the mating flanges of the mold halves to seal the parting line of the mold, or to areas within the mold where it is desired to have reinforced regions of greater wall thickness, such as ribs or bosses.
Claims19
A molding composition consisting essentially of:
- a. from 55 to 85 weight percent of thermoplastic polymer particles having a melt index less than 30 and a particle size no greater than about 40 mesh;
- and
- b. from 15 to 45 weight percent of polyethylene having a density less than 0.9 grams/cubic centimeters.
A molding composition consisting essentially of:
- a. from 55 to 85 weight percent of thermoplastic polymer particles having a melt index less than 30 and a particle size no greater than about 40 mesh;
- and
- b. from 15 to 45 weight percent of petroleum jelly.
The method of rotational molding wherein hollow-form plastic parts are formed by charging thermoplastic polymer particles to a rotational mold comprising at least two mold parts having sealing faces which mate together on a parting line to form a closed internal mold cavity, closing and heating the mold to the molding temperature of the polyolefin while rotating the mold about its major and minor axes for a time sufficient to form the molded part, cooling the mold to a demolding temperature, opening the mold and ejecting the molded part, the improvement which comprises:
- applying on a selected internal area of the mold parts at a temperature from 90 to 190 degrees F. prior to closing and heating the mold, a molding composition consisting essentially of:
- from 55 to 85 weight percent of thermoplastic polymer particles having a melt index less than 30 and a particle size no greater than about 40 mesh;
- and a carrier and binder component selected from the group consisting of petroleum jelly, very low density polyolefins, hydrocarbon waxes, hydrocarbon tackifiers and mixtures thereof in an amount from 15 to 45 weight percent of the composition.
The method of rotational molding wherein hollow-form plastic parts are formed by charging thermoplastic polymer particles to a rotational mold comprising at least two mold parts having sealing faces which mate together on a parting line to form a closed internal mold cavity, closing and heating the mold to the molding temperature of the polyolefin while rotating the mold about its major and minor axes for a time sufficient to form the molded part, cooling the mold to a demolding temperature, opening the mold and ejecting the molded part and wherein the sealing faces of the mold mate with a separation gap along at least a portion of their sealing faces, the improvement which comprises:
- applying to said portion of the sealing faces of said mold parts prior to closing and heating the mold, a molding composition consisting essentially of:
- from 55 to 85 weight percent of thermoplastic polymer particles having a melt index less than 30 and a particle size no greater than about 40 mesh;
- and a carrier and binder component selected from the group consisting of petroleum jelly, very low density polyolefins, hydrocarbon waxes, hydrocarbon tackifiers and mixtures thereof in an amount from 15 to 45 weight percent of the composition to close said gap when said mold is closed.
The method of repairing a structural void in a rotationally molded part having an open area in the wall thereof which comprises:
- a. applying a plug of a molding composition to said wall to close said open area, said molding composition consisting essentially of:
- from 55 to 85 weight percent of thermoplastic polymer particles having a melt index less than 30 and a particle size no greater than about 40 mesh;
- and a carrier and binder component selected from the group consisting of petroleum jelly, very low density polyolefins, hydrocarbon waxes, hydrocarbon tackifiers and mixtures thereof in an amount from 15 to 45 weight percent of the composition;
- and
- b. heating said plug and the wall surrounding said plug to a temperature of about 350 degrees F. to fuse said plug of molding composition into the wall of said part.
Dependencies are inferred from the claim text.