Process for polymerizing ethylene, higher alpha-olefin comonomer and dienes, especially vinyl norbornene; polymers made using such processes; and articles made from such polymers
AssigneeExxonMobil Chemical Patents Inc.
InventorPeriagaram S. Ravishankar
Life of this patent
Estimating the term…
Abstract
This invention relates to olefin polymerization processes for polymerizing ethylene, higher alpha-olefin comonomer and dienes, especially vinyl norbornene, and especially process for producing amorphous or semi-crystalline polymers such as EPDM. The invention also relates to the novel polymers produced by such processes. The invention furthermore relates to articles of manufacture with an improved balance of toughness and curing properties.
Claims11
A process for solution polymerizing ethylene, higher alpha-olefin and diene having two polymerizable double bonds, the process comprising:
- A) reacting in a first step ethylene, higher alpha-olefin comonomer and optionally one or more dienes to produce a polymer composition comprising from 0 to less than 1 mol % of diene having one or two polymerizable double bonds, in the presence of a catalyst system;
- B) reacting in a second step ethylene, higher alpha-olefin comonomer and one or more dienes at least one of which is a diene having two polymerizable double bonds in the presence of a catalyst system, the amount of diene having two polymerizable double bonds being added to the reactor in the second step being more than 50% of the total diene added in the first and second step combined;
- and
- C) recovering a polymer product having from 0.02 to 2 mol % of units derived from the diene having two polymerizable double bonds, and a branching index of greater than 0.5;
- wherein the catalyst system in one or both steps is vanadium based.
A process for solution polymerizing ethylene, higher alpha-olefin and diene having two polymerizable double bonds, the process comprising:
- A) reacting in a first step ethylene, higher alpha-olefin comonomer and optionally one or more dienes to produce a polymer composition comprising from 0 to less than 1 mol % of diene having one or two polymerizable double bonds, in the presence of a catalyst system;
- B) reacting in a second step ethylene, higher alpha-olefin comonomer and one or more dienes at least one of which is a diene having two polymerizable double bonds in the presence of a catalyst system, the amount of diene having two polymerizable double bonds being added to the reactor in the second step being more than 50% of the total diene added in the first and second step combined;
- and
- C) recovering a polymer product having from 0.02 to 2 mol % of units derived from the diene having two polymerizable double bonds, and a branching index of greater than 0.5;
- wherein the diene having two polymerizable double bonds comprises vinyl norbornene.
A process for solution polymerizing ethylene, propylene and diene having two polymerizable double bonds which comprises:
- A) reacting in a first step ethylene, propylene and optionally one or more dienes to produce a polymer composition comprising from 0 to less than 1 mol % of diene having two polymerizable double bonds, in the presence of a vanadium based catalyst system;
- B) reacting in a second step ethylene, higher alpha-olefin comonomer and diene comprising vinyl norbornene in the presence of the same catalyst system, the amount of vinyl norbornene added in the second step being more than 50% a of the total diene added in the first and second step combined;
- and
- C) recovering a polymer product having from 0.1 to 0.5 mol % of units derived from vinyl norbornene and a total of no more than 5 mol % diene derived units, from 50 to 90 mol % ethylene derived units and a balance of propylene derived units;
- a branching index of greater than 0.7, and a Mooney viscosity of from 15ML to 100 MST.