Biomedical polyurethane, its preparation and use
AssigneePolyganics B.V.
InventorsCoenraad Jan Spaans, Jacqueline Hermina de Groot, Folkert Gerhardus Dekens, Albert Johan Pennings
Life of this patent
Estimating the term…
Abstract
The invention is directed to a novel biomedical polyurethane based on diisocyanatae linked polyester polymer and diol components, said diol component having a uniform block-length.
Claims24
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, wherein the polyester component is a random copolyester component and is a copolyester component having at least two of a moiety selected from the group consisting of lactide, glycolide, trimethylene carbonate and ε-caprolactone.
A biomedical biocompatible polyurethane produced according to a process comprising the steps of (i) reacting the polyester with an isocyanate end-capped diol component in order to form a prepolymer, the ratio of isocyanate end-groups to polyester end-groups being at least 2:1, and then (ii) reacting the resulting prepolymer with water.
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, comprising from 40 up to 60% of units of lactide, based on the total number of monomeric units in the polymer.
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, comprising from 40 up to 60% of units of ε-caprolactone, based on the total number of monomeric units in the polymer.
A process for the preparation of a biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, comprising the steps of (i) reacting at least two moles of a diisocyanate with one mole of a diol selected from the group consisting of 1,4-butanediol, 1,6-hexanediol, diethyleneglycol and the reaction product of two molecules of said diol with the diisocyanate to form a first reaction product and (ii) reacting a polyester with said first reaction product.
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes a 1,4-butane diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, wherein at least 90% of the diol components, C, have the same block length and wherein the polyester component is based on (i) at least one carboxylic acid selected from the group consisting of lactic acid and succinic acid and (ii) at least one diol selected from the group consisting of ethylene glycol, 1,4-butanediol, 1,6-hexanediol and diethylene glycol.
A process for the preparation of a biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes a 1,4-butane diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, comprising the steps of (i) reacting at least 2 moles of 1,4-butane diisocyanate with 1 mole of a polyester to form a first reaction product and (ii) reacting a diol selected from the group consisting of 1,4-butanediol, 1,6-hexanediol, diethylene-glycol and the reaction product of two molecules of said diol with the 1,4-butane diisocyanate with said first reaction product.
A method for reconstruction of at least one meniscal lesion comprising the step of effecting an adhesive implant to meniscal tissue having at least one of said lesions of a meniscus-reconstructing quantity at a meniscus-reconstructing rate of at least one polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes a 1,4-butane diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, for a fibrocartilage induction time of from 10 up to 30 weeks.
A process for preparing a biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length comprising the steps of:
- i. admixing equimolar quantities of L-lactide and ε-caprolactone in the presence of a stannous octoate catalyst and a butanediol initiator thereby forming a L-lactide-ε-caprolactone prepolymer;
- ii. admixing butanediol with a six-fold excess of butane diisocyanate thereby forming an isocyanate-terminated urethane block;
- iii. dissolving the L-lactide-ε-caprolactone prepolymer in dimethyl sulfoxide to form a first solution;
- iv. dissolving the isocyanate-terminated block in dimethyl sulfoxide to form a second solution;
- v. admixing the first solution with the second solution to form a polyurethane reaction mass;
- vi. recovering the resulting urethane ploymer from the reaction mass.
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length wherein the polyester component is based on a linear random copolyester.
A biomedical biocompatible polyurethane based on (i) a diisocyanate linked polyester polymer component and (ii) a diol component, said polyurethane having the formula [Parenopenst]A—B—C—B[Parenclosest]n wherein A denotes said polyester component, B denotes said diisocyanate moiety, C denotes said diol component, n denotes the number of recurring units, and wherein at least 90% of the diol components, C, have the same block length, wherein the polyester component is based on a linear random copolyester, said biocompatible polyurethane having a phase separated morphology, comprising (i) soft segments consisting of polyester components and (ii) urethane-based hard segments of uniform size, said hard segments consisting of diol components having a uniform block-length, and wherein the diol components and the polyester components have been linked to a diisocyanate component by means of reaction thereof with a diisocyanate.
Dependencies are inferred from the claim text.