Aluminum alloy for making naturally aged die cast products

Abstract

Aluminum alloy die castings combine good as-cast strength with good as-cast ductility, without any heat treatment. The alloy comprises 2.75 5.25 wt. % magnesium, 1.85-3.15 wt. % zinc, 0.65-1.2 wt. % manganese, 0.10-0.18 wt. % iron, less than 0.10 wt. % copper, less than 0.10 wt. % silicon, less than 0.20 wt. % titanium and the balance aluminum and incidental impurities and furthermore the percent by weight magnesium is greater than or equal to the percent by weight zinc. A particularly high strength version of the alloy comprises 4.75%-5.25 wt. % magnesium and 2.85-3.15 wt. % zinc. A particularly high ductility version of the alloy comprises 2.75-3.25 wt. % magnesium, 1.85 2.5 wt. % zinc.