Easy to disperse, high durability TiO2 pigment and method of making same
AssigneeE. I. Du Pont de Nemours and Company
InventorsCharles Robert Bettler, Michael Patrick Deibold
Life of this patent
Estimating the term…
Abstract
The present invention relates to a TiO2 pigment coated sequentially in a wet treatment process with hydrous silica and hydrous alumina both in the presence of citric acid wherein the resulting pigment is coated with from 1 to 4% amorphous alumina based on the weight of the untreated TiO2; from 3 to 6% silica glass based on the weight of the untreated TiO2.
Claims8
A method for making an easy-dispersing, high durability titanium dioxide pigment comprising the steps in sequence:
- A.
- (1) heating a slurry of titanium dioxide particles to a temperature of from 85 to 100° C.,
- (2) adding citric acid to the slurry to form a mixture,
- (3) adjusting the pH of the mixture to 10 or more,
- (4) adding sufficient sodium silicate as a water solution to the mixture to deposit silica on the surface of the particles of from 1 to 6% based on the weight of the titanium dioxide particles in the slurry,
- (5) neutralizing the slurry by addition of a mineral acid over the course of one hour, thereby forming a slurry of silica coated titanium dioxide particles;
- and
- B.
- (1) adjusting the temperature of the slurry of silica coated titanium dioxide particles to a temperature of from 55 to 90° C.,
- (2) adding sufficient sodium aluminate as a water solution to the slurry in step B(1) and adjusting the pH of the mixture formed to from 5 to 9 by addition of a strong mineral acid to deposit aluminia as Al2O3 of from 1 to 4% by weight based on the weight of titanium dioxide particles present in the slurry of step A(1) on the surface of the silica coated particles, and digesting the resulting mixture for from 15 to 30 minutes.
An improved method of making a titanium dioxide particles wherein the particles in a water slurry are wet treated with water solution of sodium silicate and sodium aluminate to form titanium dioxide having a first coating of silica followed by a second coating of aluminia wherein the improvement comprises adding citric acid to the titanium dioxide slurry before the addition of sodium silicate solution.