Ferrite core and its production method

Abstract

A ferrite core is provided. This ferrite core has high saturation flux density Bs at a high temperature of 100° C. or higher, and in particular, at around 150° C., and has excellent magnetic stability at a high temperature, experiencing reduced deterioration of magnetic properties, and in particular, reduced core loss at such high temperature (even by trading off some improvement in the level of the loss). The ferrite core of the invention contains 55 to 59 mol % of iron oxide calculated in terms of Fe2O3, more than 0 to 15 mol % of zinc oxide calculated in terms of ZnO, 2 to 10 mol % of nickel oxide calculated in terms of NiO, and the balance of manganese oxide (MnO) as its main components, and when the main components has a composition represented by the formula: (Zn2+a, Ni2+b, Mn2+c, Mn3+d, Fe2+e, Fe3+f)O4+δ  (1) wherein a, b, c, d, e and f meet the relations: a+b+c+d+e+f=3, and δ=a+b+c+(3/2)d+e+(3/2)f−4 the value of δ in formula (1) is such that: 0≦δ≦2.5×10−3.