Alumina fiber aggregate and its production method

Abstract

An alumina fiber aggregate comprising alumina short fibers whose average diameter is 4.0 to 10.0 μm and smallest diameter is not less than 3.0 μm, and a method of producing an alumina fiber aggregate which comprises spinning a spinning solution containing basic aluminum chloride, a silicon compound, an organic polymer and water by the blowing method, and calcining the obtained aggregate of alumina short fiber precursor, the spinning solution being one in which the aluminum/silicon ratio is 99/1 to 65/35 calculated as Al2O3/SiO2 ratio by weight, the concentration of basic aluminum chloride is 180 to 200 g/L and the concentration of the organic polymer is 20 to 40 g/L. The alumina short fibers in the alumina fiber aggregate are enlarged in diameter to suppress scattering of the fibers.