Abstract
Cellulosic materials such as wood chips, textile fibers and the like are treated to produce products such as particle board having enhanced fire and heat resistant properties. For example, wood chips are saturated with an eqimolar aqueous solution of monoammonium phosphate and diammonium phosphate. A metal hydroxide is added to the solution. The saturated wood chips are dried and mixed with a modified glue composition. The glue that which contains urea formaldehyde and/or phenolic resin is in powdered form and dissolved in water. The treated wood chips and modified glue is then mixed, formed into a mat and placed under pressure at about 120° C. for 8 to 15 minutes. The pressure may range from about 300 to 400 psi.
Claims16
A method for producing a fire retardant cellulosic sheet material comprising the steps of:
- a) provide an aqueous solution of diammonium phosphate and monoammonium phosphate having a concentration of between about 0.325 and 1.0 moles per liter of diammonium phosphate and between 0.325 and 1.0 moles per liter of monoammonium phosphate and wherein the molar concentration of diammonium phosphate and monoammonium phosphate are about equal;
- b) adding a metal hydroxide to the solution of step a) in an amount between about 0.325 and 1.0 moles per liter to thereby provide a modified solution;
- c) providing a mass of cellulosic material and adding about 450 to 550 grams of cellulosic material per liter to the modified solution from step b);
- d) saturating the mass of cellulosic material with the modified solution of step b) by stirring until the mix reaches a uniform dark brown color;
- e) drying the saturated cellulosic material at a temperature between about 105 and 130 degrees C. until the cellulosic material has a uniform tan color and a moisture content of about 15%;
- f) providing a mass of glue;
- g) mixing the glue with a solution of monoammonium phosphate and diammonium phosphate to thereby provide a treated glue;
- h) mixing the dried saturated cellulosic material from step e) with the treated glue from step g);
- and
- i) heating the mixture of the dried saturated cellulosic material and treated glue from step h) at a temperature of about 120° C. to 195° C. under a pressure of about 350 to 400 psi to thereby provide a fire retardant particle board with enhanced flame and heat resistance.
A method for producing a fire retardant cellulosic sheet material comprising the steps of:
- a) provide an aqueous solution of diammonium phosphate and monoammonium phosphate having a concentration of between about 0.325 and 1.0 moles per liter of diammonium phosphate and between 0.325 and 1.0 moles per liter of monoammonium phosphate and wherein the molar concentration of diammonium phosphate and monoammonium phosphate are about equal;
- b) adding a metal hydroxide to the solution of step a) in an amount between about 0.325 and 1.0 moles per liter to thereby provide a modified solution;
- c) providing a mass of cellulosic material and adding about 450 to 550 grams of cellulosic material per liter to the modified solution from step b);
- d) saturating the mass of cellulosic material with the modified solution of step b) by vigorous agitation for about 10 to 15 minutes at a temperature of about 20° C. to about 25° C. until the cellulosic material takes on a uniform dark brown color;
- e) drying the saturated cellulosic material at a temperature between about 105 degrees C. to about 120° C. for about 45 to about 70 minutes with stirring until the cellulosic material has a uniform tan color and a moisture content of about 15%;
- f) providing a mass of glue;
- g) mixing the glue with a solution of monoammonium phosphate and diammonium phosphate from step a) for a period of 10 to 15 minutes to thereby provide a treated glue;
- h) mixing the dried saturated cellulosic material from step e) with the treated glue from step g);
- and
- i) heating the mixture of the dried saturated cellulosic material and treated glue from step h) at a temperature of about 120° C. to 195° C. under a pressure of about 350 to 400 psi to thereby provide a fire retardant particle board with enhanced flame and heat resistance.
Dependencies are inferred from the claim text.