Glaze for ceramic superplastic forming (SPF) dies
AssigneeThe Boeing Company
InventorsDaniel G. Sanders, Martin A. Peterson, David C. Van Aken, D. Trent Weaver, F. Scott Miller, Jeffrey D. Smith
Life of this patent
Estimating the term…
Abstract
The life of ceramic SPF dies can be enhanced significantly by plasma spray application of a cordierite glaze on the forming surface. The preferred glaze has a coefficient of thermal expansion close to or matching with the ceramic of the die, and, typically, is a 2•2•5 MAS system including 2-10 mol % TiO2 (or above 8 wt %).
Claims14
A method for improving the life of a ceramic die made from a refractory concrete and subject to extended exposure to elevated temperatures in a metal forming operations the die having a forming surface, comprising the step of:
- applying a glaze to the forming surface to harden the surface and to provide thermal shock resistance, the glaze having a coefficient of thermal expansion (CTE) substantially matching that coefficient of thermal expansion for the ceramic die achieved by adding 4-8 mol % of titanium oxide to the glaze and the glaze also having a high glass transformation temperature of at least about 800° C. suitable for the metal forming operation.
A ceramic die having a forming surface coated with a toughening cordierite glaze at least on the die's forming surface to enhance the life of the die in SPF operations by hardening the die and providing thermal shock resistance, the cordierite glaze including titanium oxide for adjusting the coefficient of thermal expansion of the glaze to match that of the die,
- wherein the die is a refractory concrete, the glaze is 2-2-5 MAS cordierite glass, and the amount of titanium oxide in the glaze is 4-8 mol %.