Material on an aluminum basis for anti-friction bearings
AssigneeKS Gleitlager GmbH
InventorsKarl-Heinz Matucha, Thomas Steffens, Werner Schubert
Life of this patent
Estimating the term…
Abstract
An aluminum-based material for anti-friction bearings composed of an aluminum alloy with 10-25 wt % tin or 5-25 wt % lead, impurity-caused components characterized by 0.75-2.5 wt % iron and an alloy additive capable of forming an intermetallic compound having a spherical phase homogeneously distributed in the aluminum alloy. The alloy additive is one of: a) manganese and silicon, in which the weight percentage fractions of manganese and silicon are at least half the weight percentage fraction of the iron and for manganese, at most 3 wt %, and for silicon, at most 2 wt %; b) 0.1-0.5 wt % cobalt; and c) 0.1-0.5 wt % molybdenum.
Claims6
An aluminum-based material for anti-friction bearings, the material consisting essentially of:
- an aluminum alloy with 10-25 wt % tin;
- impurity-caused components, the impurity-caused components characterized by 0.8-1.2 wt % iron and;
- an alloy additive capable of forming an intermetallic compound having a spherical phase homogeneously distributed in the aluminum alloy, the alloy additive selected from the group consisting of:
- a) manganese and silicon, wherein the individual weight percentage fractions of manganese and silicon are at least half the weight percentage fraction of the iron and for manganese, 0.4-0.6 wt %, and for silicon, 0.4-0.6 wt %;
- b) 0.1-0.5 wt % cobalt;
- and
- c) 0.1-0.5 wt % molybdenum;
- wherein the intermetallic compound formed by the alloy additive is at least one of iron-manganese-aluminum-silicon complexes, iron-cobalt mixed aluminides and iron molybdenum-mixed aluminides.
An aluminum-based material for anti-friction bearings, consisting of:
- an aluminum alloy with 10-25 wt % tin;
- impurity-caused components, the impurity-caused components characterized by 0.75-2.5 wt % iron;
- and
- an alloy additive of manganese and silicon, wherein the individual weight percentage fractions of manganese and silicon are at least half the weight percentage fraction of the iron and for manganese, at most 3 wt %, and for silicon, at most 2 wt %, the alloy additive capable of forming an intermetallic compound having a spherical phase homogeneously distributed in the aluminum alloy, wherein the intermetallic compound is of an iron-manganese-aluminum-silicon complex.