Aluminum nitride/aluminum base composite material and method of producing the same
AssigneeSony Corporation
InventorsShingo Kadomura, Kei Takatsu, Shinsuke Hirano, Nobuyuki Suzuki
Life of this patent
Estimating the term…
Abstract
A method for producing an aluminum nitride/aluminum base composite material comprising the steps of; (A) charging aluminum nitride powder into a container provided in a molten metal pressure apparatus, (B) applying pressure to the aluminum nitride powder in the container, (C) pouring a molten aluminum base material into the container, and, (D) applying pressure to the molten aluminum base material in the container to fill the aluminum base material in space between the aluminum nitride powder particles.
Claims16
A method for producing an aluminum nitride/aluminum base composite material comprising the steps of:
- (A) charging aluminum nitride powder particles into a container provided in a molten metal pressure apparatus;
- (B) applying pressure to the aluminum nitride powder particles in the container;
- (C) pouring a molten aluminum base material into the container;
- and,
- (D) applying pressure to the molten aluminum base material in the container to fill the aluminum base material in a space between the aluminum nitride powder particles.
A method for producing an aluminum nitride/aluminum base composite material comprising the steps of:
- (a) charging aluminum nitride powder particles into a container provided in a molten metal pressure apparatus;
- (b) applying pressure to the aluminum nitride powder particles in the container;
- (c) pouring a molten aluminum base material into the container;
- (d) applying pressure to the molten aluminum base material in the container to fill the aluminum base material in a space between the aluminum nitride powder particles, thereby obtaining a base material;
- and
- (e) covering a surface of the base material with a covering layer consisting of a ceramic material.
A method for producing an aluminum nitride/aluminum base composite material comprising the steps of:
- (A) preparing a preform having pores obtained by sintering aluminum nitride powder;
- (B) enclosing the preform in a container provided in a molten metal pressure apparatus;
- (C) pouring a molten aluminum base material into the container together with silicon lumps;
- and,
- (D) applying pressure to the molten aluminum base material in the container to fill the aluminum base material in the pores of the preform.
A method for producing an aluminum nitride/aluminum base composite material comprising the steps of:
- (a) preparing a preform having pores, obtained by sintering aluminum nitride powder, where a particle size of said aluminum nitride powder is in a range from 10 to 100 μm;
- (b) enclosing the preform in a container provided in a molten metal pressure apparatus;
- (c) pouring a molten aluminum base material into the container;
- (d) applying pressure to the molten aluminum base material in the container to fill the aluminum base material in the pores of the preform, thereby obtaining a base material;
- and
- (e) covering the surface of the base material with a covering layer consisting of a ceramic material wherein the molten aluminum base material is poured into the container together with silicon lumps.
An aluminum nitride/aluminum base composite material, which comprises:
- (a) a composite material obtained by charging aluminum nitride powder particles into a container provided in a molten metal pressure apparatus, applying pressure to the aluminum nitride powder particles in the container, pouring a molten aluminum base material into the container, and applying pressure to the molten aluminum base material in the container to fill the aluminum base material in a space between the aluminum nitride powder particles;
- and
- (b) a covering layer, consisting of a ceramic material comprising aluminum and TiO2, and covering a surface of the composite material.