Penetration flux

Abstract

Deep penetration gas tungsten arc welds are achieved using titanates such as Na2Ti3O7 or K2TiO3. A small amount of the titanate is applied to the weld zone in a carrier fluid paste or as part of a wire filler to afford deep penetration welds in carbon, chrome-molybdenum, and stainless steels as well as nickel-based alloys. To control arc wander, bead consistency, and slag and surface appearance of the weldments, various additional components may be optionally added to the titanate flux including transition metal oxides such as TiO, TiO2, Cr2O3, and Fe2O3, silicon dioxide, manganese silicides, fluorides and chlorides. However, the toxicity of the plumes from halide additives and the necessity of post-weld removal to prevent corrosion may preclude their use. In addition, it was found that a flux of titanium oxides, Fe2O3 and Cr2O3 affords deep weld penetration in carbon steels and nickel-based alloys but with some heat-to-heat variation.