Method of forming ruthenium interconnect for an integrated circuit
AssigneeMicron Technology, Inc.
InventorsTongbi Jiang, Li Li
Life of this patent
Estimating the term…
Abstract
A multi-layered metal bond pad for a semiconductor die having a conductive metal layer and an overlying ruthenium electrode layer. The ruthenium electrode layer protects the conductive metal from oxidation due to ambient environmental conditions. An interconnect structure such as a wire bond or solder ball may be attached to the ruthenium layer to connect the semiconductor die to a lead frame or circuit support structure. Also disclosed are processes for forming the ruthenium layer.
Claims30
A method of forming a ruthenium interconnect, comprising the steps of:
- providing a bond pad having a layer of an ambient oxidizable metal;
- providing an aqueous ruthenium hydroxide solution;
- and
- exposing the bond pad to said aqueous ruthenium solution for a sufficient time to form a ruthenium layer of a desired thickness on the bond pad.
A method of forming a ruthenium interconnect, comprising the steps of:
- providing a semiconductor die having at least one bond pad, wherein said at least one bond pad includes an ambient oxidizable metal layer and a metal oxide layer on the ambient oxidizable metal layer;
- removing said metal oxide layer;
- providing an aqueous ruthenium hydroxide solution;
- and
- exposing said at least one bond pad to said aqueous ruthenium hydroxide solution for a sufficient time to form a ruthenium layer of a desired thickness on said at least one bond pad.
A method of forming a ruthenium interconnect, comprising the steps of:
- providing a semiconductor die having at least one bond pad, wherein said at least one bond pad includes an ambient oxidizable metal layer and a metal oxide layer on the ambient oxidizable metal layer;
- providing an aqueous acid solution;
- removing said metal oxide layer by exposing said at least one bond pad to the aqueous acid solution;
- providing an aqueous ruthenium hydroxide solution;
- and
- exposing said at least one bond pad to said ruthenium hydroxide solution until a ruthenium layer of a desired thickness is formed on said at least one bond pad.
A method of forming a ruthenium interconnect, comprising the steps of:
- providing a semiconductor die having at least one bond pad, wherein said at least one bond pad has an ambient oxidizable metal layer and a metal oxide layer on the ambient oxidizable metal layer;
- providing an aqueous solution comprising an acid and ruthenium hydroxide;
- providing an electric current to the aqueous solution;
- and
- exposing said at least one bond pad to the aqueous solution for a predetermined time until the metal oxide layer has been removed and a ruthenium layer of a desired thickness is formed on said at least one bond pad.