Method for manufacturing printed wiring board comprising electrodeposited copper foil with carrier and resistor circuit; and printed wiring board comprising resistor circuit

A printed wiring board comprising a composite copper foil which comprises a carrier, a nickel alloy layer for forming a resistor circuit, wherein said nickel alloy layer consists essentially of nickel and at least one component selected from the group consisting of phosphorus, boron, sulfur, titanium, vanadium, chromium, manganese, iron, cobalt, zinc, molybdenum, tungsten, tin and antimony, and a copper foil layer having copper microparticles deposited opposite to the side having said nickel alloy layer, wherein the thickness of said nickel alloy layer is 0.01 μm to 4 μm, said printed wiring board is obtained by:

• forming a copper etching resist layer on the surface of said copper foil for forming the circuit of the composite copper foil with a carrier, and exposing and developing the circuit pattern of the copper foil circuits to be formed on said copper etching resist layer,
• forming the copper foil circuits by etching the copper foil for forming the circuit using a copper etching solution that does not dissolve the nickel alloy layer,
• removing the copper etching resist layer,
• fabricating a copper clad laminate by laminating and hot-pressing the composite copper foil with the carrier and a material for composing an insulating layer in the state where the surface of the composite copper foil with a carrier on which the copper foil circuits are formed contacts the insulating layer composing material,
• removing the carrier positioned on the outer layer of said copper clad laminate to expose the nickel alloy layer for forming the resistor circuit,
• forming a nickel etching resist layer on said nickel alloy layer, and exposing and developing the resistor circuit pattern,
• forming the resistor circuit by using an etching solution for nickel alloy, and
• removing the nickel etching resist layer.

A method for manufacturing a printed wiring board with resistor circuits comprising copper foil circuits and resistor circuits, said method using a composite copper foil which comprises a carrier, a nickel alloy layer for forming a resistor circuit, wherein said nickel alloy layer consists essentially of nickel and at least one component selected from the group consisting of phosphorus, boron, sulfur, titanium, vanadium, chromium, manganese, iron, cobalt, zinc, molybdenum, tungsten, tin and antimony, and a copper foil layer having copper microparticles disposed opposite to the side having said nickel alloy layer, wherein the thickness of said nickel alloy layer is 0.01 μm to 4 μm, and said method comprising the steps of:

• forming a copper etching resist layer on the surface of said copper foil for forming the circuit of the composite copper foil with a carrier, and exposing and developing the circuit pattern of the copper foil circuits to be formed on said copper etching resist layer,
• forming the copper foil circuits by etching the copper foil for forming the circuit using a copper etching solution that does not dissolve the nickel alloy layer,
• removing the copper etching resist layer,
• fabricating a copper clad laminate by laminating and hot-pressing the composite copper foil with a carrier and a material for composing an insulating layer in the state where the surface of the composite copper foil with a carrier on which the copper foil circuits are formed contacts the insulating layer composing material,
• removing the carrier positioned on the outer layer of said copper clad laminated to expose the nickel alloy layer for forming the resistor circuit,
• forming a nickel etching resist layer on said nickel alloy layer, and exposing and developing the resistor circuit pattern,
• forming the resistor circuit by using an etching solution for nickel alloy, and
• removing the nickel etching resist layer.

A method for manufacturing a printed wiring board with resistor circuits comprising copper foil circuits and resistor circuits, comprising forming a composite copper foil with a carrier comprising a nickel alloy layer between a copper carrier and a copper foil layer wherein said nickel alloy layer consists essentially of nickel and at least one component selected from the group consisting of phosphorus, boron, sulfur, titanium, vanadium, chromium, manganese, iron, cobalt, zinc, molybdenum, tungsten, tin and antimony, and said copper foil layer having copper microparticles disposed opposite to the side having said nickel alloy layer, wherein the thickness of said nickel alloy layer is 0.01 μm to 4 μm, the method comprising the steps of:

• forming a copper etching resist layer on a surface of said copper foil for forming the circuit of the composite copper foil with a carrier, and exposing and developing a circuit pattern of the copper foil circuits to be formed on said copper etching resist layer,
• forming the copper foil circuits by etching the copper foil for forming the circuit using a copper etching solution that does not dissolve the nickel alloy layer,
• removing the copper etching resist layer,
• fabricating a copper clad laminate by laminating and hot-pressing the composite copper foil with a carrier and a material for composing an insulating layer in the state where the surface of the composite copper foil with a carrier on which the copper foil circuits are formed contacts the insulating layer material,
• removing the copper carrier positioned on the outer layer of said copper clad laminate to reveal the nickel alloy layer for forming the resistor circuit,
• forming a nickel etching resist layer on said nickel alloy layer, and exposing and developing a resistor circuit pattern on the nickel etching resist layer,
• forming a resistor circuit by etching the nickel alloy layer using an etching solution for nickel alloy, and
• removing the nickel etching resist layer.

A printed wiring board comprising a composite copper foil which comprises a copper carrier, a copper foil layer comprising copper microparticles which have been deposited on a surface of the copper foil layer, and a nickel alloy layer between the copper carrier and the copper foil layer wherein said nickel alloy layer consists essentially of nickel and at least one component selected from the group consisting of phosphorus, boron, sulfur, titanium, vanadium, chromium, manganese, iron, cobalt, zinc, molybdenum, tungsten, tin and antimony, wherein the thickness of said nickel alloy layer is 0.01 μm to 4 μm, said printed wiring board is obtained by:

• forming a copper etching resist layer on a surface of said copper foil for forming the circuit of the composite copper foil with a carrier, and exposing and developing a circuit pattern of the copper foil circuits to be formed on said copper etching resist layer,
• forming the copper foil circuits by etching the copper foil for forming the circuit using a copper etching solution that does not dissolve the nickel alloy layer,
• removing the copper etching resist layer,
• fabricating a copper clad laminate by laminating and hot-pressing the composite copper foil with a carrier and a material for composing an insulating layer in the state where the surface of the composite copper foil with a carrier on which the copper foil circuits are formed contacts the insulating layer material,
• removing the copper carrier positioned on the outer layer of said copper clad laminate to reveal the nickel alloy layer for forming the resistor circuit,
• forming a nickel etching resist layer on said nickel alloy layer, and exposing and developing a resistor circuit pattern on the nickel etching resist layer,
• forming a resistor circuit by etching the nickel alloy layer using an etching solution for nickel alloy, and
• removing the nickel etching resist layer.