Aluminum alloy with intergranular corrosion resistance and methods of making and use
OwnerBaolute Reninventor
Life of this patent
Estimating the term…
Abstract
A corrosion resistant aluminum alloy has controlled amounts of iron, manganese, chromium, and titanium along with levels of copper, silicon, nickel, and no more than impurity levels of zinc. The alloy chemistry is tailored such that the electrolytic potential of the grain boundaries matches the alloy matrix material to reduce intergranular corrosion. The alloy is particularly suited for the manufacture of tubing for heat exchangers using extrusion and brazing techniques.
Claims9
In a method of making an aluminum alloy having corrosion resistance, wherein an alloy is melted and at least cast to a shape having a composition consisting essentially of, in weight percent:
- between about 0.05 and 0.5% silicon;
- an amount of iron between about 0.05% and up to 0.7%;
- an amount of manganese up to about 2.0%;
- an amount of zinc;
- up to about 0.10% magnesium;
- up to about 0.10% nickel;
- up to about 0.5% copper;
- up to about 0.50% chromium;
- between about 0.03 and 0.35% titanium;
- with the balance aluminum and inevitable impurities;
- wherein the manganese to iron ratio is maintained between about 2.0 and about 6.0, the improvement comprising controlling the amount of zinc, chromium, titanium when making the alloy, such that the zinc amount is less than 0.06%, chromium is between 0.03 and 0.35%, and the ratio of chromium to titanium is controlled to between about 0.25 and 2.0.
In a method of making a heat exchanger wherein a plurality of tubes are brazed to fin stock, the improvement comprising making the tubes from an aluminum alloy having a composition consisting essentially of, in weight percent:
- between about 0.05 and 0.5% silicon;
- an amount of iron between about 0.05% and up to 0.7%;
- an amount of manganese up to about 2.0%;
- less than about 0.6% zinc;
- up to about 0.10% magnesium;
- up to about 0.10% nickel;
- up to about 0.5% copper;
- between alum about 0.03 and 0.50% chromium;
- between about 0.03 and 0.35% titanium;
- with the balance aluminum and inevitable impurities;
- wherein the manganese to iron ratio is maintained between about 2.0 and about 6.0, and the amounts of chromium and titanium are controlled so that a ratio of chromium to titanium ranges between 0.25 and 2.0.
Dependencies are inferred from the claim text.