Semiconductor device and production method thereof

Abstract

The present invention provides a MOS semiconductor device which enables gate leakage current reduction with a thinner gate dielectric film for higher speed, and a production method thereof. According to the present invention, a gate dielectric film 6 is made as follows: after forming a silicon nitride film 3 with a specified thickness, it is annealed in an oxidizing atmosphere to form silicon oxide 4 on the silicon nitride film 3, then this silicon oxide 4 is completely removed by exposure to a dissolving liquid. As a result, at depths between 0.12 nm and 0.5 nm from the top surface of the silicon nitride film 3 in the gate dielectric film 6 whose main constituent elements are silicon, nitrogen and oxygen, the nitrogen concentration is higher than the oxygen concentration. This enables the use of a thinner gate dielectric film with silicon, nitrogen and oxygen as main constituent elements while at the same time realizing reduction in leakage currents.