Back to results
US 6,646,098 B2Granted
Polycarbonate resin molding material for optical use and optical disk substrate
AssigneeTeijen Chemicals
InventorYutaka Dohi
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeTeijen Chemicals
InventorYutaka Dohi
Estimating the term…
The present invention relates to a polycarbonate resin molding material for optical use which contains substances (A) having a 5% weight reduction start temperature measured by thermogravimetric analysis of 400° C. or less in a total amount of 1 wt % or less and to a polycarbonate resin molding material for optical use which contains substances (A) having a 5% weight reduction start temperature measured by thermogravimetric analysis of 400° C. or less in a total amount of 1 wt % or less and a sodium compound in an amount of 1 ppm or less in terms of metal sodium. The present invention also relates to optical disk substrates formed from these molding materials. According to the present invention, use of each of the above molding materials makes possible the continuous molding of an optical disk substrate and the obtained optical disk substrate has high quality and can retain reliability for a long time as an optical disk for a high-density recording medium.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, which contains substance (A) having a 5% weight reduction start temperature measured by thermogravimetric analysis of 400° C. or less in a total amount of 0.5 wt % or less and which has a viscosity average molecular weight of 10,000 to 22,000.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, wherein when 10,000 optical disk substrates are molded at a cylinder temperature of 340° C. and a mold temperature of 75° C., the amount of a deposit on a stamper is 15 mg or less.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, wherein when 10,000 optical disk substrates are molded at a cylinder temperature of 380° C. and a mold temperature of 115° C., the amount of a deposit on a stamper is 15 mg or less.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, which contains substance (A) having a 5% weight reduction start temperature measured by thermogravimetric analysis of 400° C. or less in a total amount of 0.5 wt % or less and a sodium compound in an amount of 1 ppm or less in terms of metal sodium and which has a viscosity average molecular weight of 10,000 to 20,000.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, wherein (1) when 10,000 CD optical disk substrates are molded at a cylinder temperature of 340° C. and a mold temperature of 75° C., the amount of a deposit on a stamper is 15 mg or less and (2) the number of white point defects of 20 μm or more in size is 2 or less per a 120 mm diameter disk-like substrate after an acceleration deterioration test (80° C.×85% RH×1,000 hours) on the optical disk substrates.
A polycarbonate resin molding material for optical use, which contains a stabilizer and a release agent, wherein (1) when 10,000 DVD optical disk substrates are molded at a cylinder temperature of 380° C. and a mold temperature of 115° C., the amount of a deposit on a stamper is 15 mg or less and (2) the number of white point defects of 20 μm or more in size is 2 or less per a 120 mm diameter disk-like substrate after an acceleration deterioration test (80° C.×85% RH×1,000 hours) on the optical disk substrates.