Polymer composition
AssigneeLucite International UK Limited
InventorsMichael Stephen Chisholm, Andrew Trevithick Slark, David Sherrington, Nial O'Brien
Life of this patent
Estimating the term…
Abstract
Branched polymers are prepared by mixing together monofunctional vinylic monomer with from 0.3 to 100% w/w of polyfunctional vinylic monomer and from 0.0001 to 50% w/w of chain transfer agent and thereafter reacting the mixture to form a polymer. The resulting branched polymers are soluble and may be used as component of surface coatings and inks as well as molding resins.
Claims11
A method for preparing a branched copolymer, which comprises,
- (i) mixing together a monofunctional monomer having one polymerizable double bond per molecule with from 0.5-50% w/w (of the weight of the monfunctional monomer) of a polyfunctional monomer having at least two polymerizable double bonds per molecule and from 0.001-50% w/w (of the weight of the monofunctional monomer) of a chain transfer agent;
- (ii) dispersing the resulting mixture as a discontinuous phase in a continuous phase in which the monomers are relatively insoluble in the presence of a dispersing agent which is capable of maintaining the mixture of monomers as a discontinuous phase in the continuous phase;
- (iii) initiating polymerization of the monomer mixture;
- (iv) maintaining the dispersion of monomer in continuous phase at reaction temperature for sufficient time to enable the monomers to react to form a polymer;
- and
- (v) subsequently separating the dispersed phase containing the polymer from the continuous phase.
A method of preparing a branched polymer comprising mixing together a monofunctional monomer comprising at least a methacrylate monomer, said monofunctional monomer having one polymerisable double bond per molecule, with from 0.5-100% w/w, based on the weight of the monofunctional monomer, of a polyfunctional monomer having at least two polymerisable double bonds per molecule and from 0.0001-0.5% w/w, based on the weight of the monofunctional monomer, of a catalytic chain transfer agent and optionally a free-radical polymerisation initiator and thereafter reacting said mixture to form said polymer.
A method for preparing a branched copolymer, which comprises,
- (i) mixing together a monofunctional monomer having one polymerizable double bond per molecule with from 0.5-50% w/w (of the weight of the monfunctional monomer) of a polyfunctional monomer having at least two polymerizable double bonds per molecule and from 0.0001-0.5% w/w (of the weight of the monofunctional monomer) of a catalytic chain transfer agent;
- (ii) dispersing the resulting mixture as a discontinuous phase in a continuous phase in which the monomers are relatively insoluble in the presence of a dispersing agent which is capable of maintaining the mixture of monomers as a discontinuous phase in the continuous phase;
- (iii) initiating polymerization of the monomer mixture;
- (iv) maintaining the dispersion of monomer in continuous phase at reaction temperature for sufficient time to enable the monomers to react to form a polymer;
- and
- (v) subsequently separating the dispersed phase containing the polymer from the continuous phase.
A method of preparing a branched polymer comprising mixing together a monofunctional monomer at least comprising a methacrylate monomer, said monofunctional monomer having one polymerisable double bond per molecule with from 0.5-100% w/w, based on the weight of the monofunctional monomer, of a polyfunctional monomer having at least two polymerisable double bonds per molecule and from 0.0001-50% w/w, based on the weight of the monofunctional monomer, of a chain transfer agent comprising a monofunctional thiol or a polyfunctional thiol and optionally a free-radical polymerisation initiator and thereafter reacting said mixture to form said polymer, wherein the weight average molecular weight (Mw) of the branched polymer is in the range of 2,000 to 200,000.
A method of preparing a branched polymer comprising mixing together a monofunctional monomer at least comprising a methacrylate monomer, said monofunctional monomer having one polymerisable double bond per molecule with from 0.5-100% w/w, based on the weight of the mono functional monomer, of a polyfunctional monomer having at least two polymerisable double bonds per molecule and from 0.0001-50% w/w, based on the weight of the monofunctional monomer, of a chain transfer agent comprising a monofunctional thiol or a polyfunctional thiol and optionally a free-radical polymerisation initiator and thereafter reacting said mixture to form said polymer, wherein the polyfunctional monomer is at least one monomer selected from the group consisting of ethylene glycol di(meth)acrylate, tripropylene glycol di(meth)acrylate, butanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylenene glycol di(meth)acrylate, dipropylene glycol diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, dipropylene glycol di(meth)acrylate, allyl (meth) acrylate, divinyl benzene, tripropylene glycol tri(meth)acrylate, trimethylol propane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate and dipentaerythritol hexa(meth)acrylate.
A method of preparing a branched polymer comprising mixing together a monofunctional monomer comprising at least a methacrylate monomer, said monofunctional monomer having one polymerisable double bond per molecule, with from 0.5-100% w/w, based on the weight of the monofunctional monomer, of a polyfunctional monomer having at least two polymerisable double bonds per molecule and from 0.0001-50% w/w, based on the weight of the monofunctional monomer, of a chain transfer agent comprising a monofunctional thiol or a polyfunctional thiol and optionally a free-radical polymerisation initiator and thereafter reacting said mixture to form said polymer.
Dependencies are inferred from the claim text.