Method for fabricating plated products
AssigneeToyoda Gosei Co., Ltd.
InventorsYukitaka Hasegawa, Yousuke Maruoka, Yasuhiko Ogisu
Life of this patent
Estimating the term…
Abstract
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base is provided. The method includes the step of forming the basecoat layer and the metal plating layer on the surface of the base. The step is followed by subjecting the metal plating layer to a cold heat treatment or an ultrasonic wave treatment, thus forming a microcrack in the metal plating layer. Afterwards, the topcoat layer is formed on the surface of the metal plating layer.
Claims12
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, the method comprising the steps of:
- forming the basecoat layer and the metal plating layeron the surface of the base;
- forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment after the formation of the basecoat layer and the metal plating layer, wherein the cold heat treatment is performed by repeating a plurality of treatment cycles, and each of the treatment cycles includes cooling the metal plating layer to −20 degrees Celsius or lower and then heating the metal plating layer to 60 degrees Celsius or higher;
- and
- forming the topcoat layer on a surface of the metal plating layer.
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, the method comprising the steps of:
- forming the basecoat layer and the metal plating layer on the surface of the base;
- forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or a supersonic wave treatment after the formation of the basecoat layer and the metal plating layer;
- applying a solution in which ultra-fine particles of an inorganic oxide are dispersed on the surface of the metal plating layer after the formation of the microcrack in the metal plating layer;
- and
- forming the topcoat layer on a surface of the metal plating layer.
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, wherein the metal plating layer is a silver plating layer formed by a chemical plating method that uses silver mirror reaction, the method comprising the steps of:
- forming the basecoat layer and the metal plating layer on the surface of the base;
- forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or a supersonic wave treatment after the formation of the basecoat layer and the metal plating layer;
- and
- forming the topcoat layer on a surface of the metal plating layer.
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base formed of synthetic resin, the method comprising the steps of:
- forming the basecoat layer on the surface of the base, wherein the basecoat layer is obtained by applying a basecoat agent to the surface of the base or immersing the surface of the base in the basecoat agent and then drying the basecoat agent on the surface of the base;
- forming the metal plating layer on the basecoat layer, wherein the metal plating layer is obtained by a chemical silver plating method;
- forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or an ultrasonic wave treatment;
- and
- forming the topcoat layer on the surface of the metal plating layer.