US 6,642,162 B2Granted
Glass composition for crystallized glass
AssigneeMinolta Co., Ltd.
InventorsHideki Nagata, Hiroshi Yuki, Toshiharu Mori, Hideki Kawai, Kazuhiko Ishimaru
Life of this patent
Estimating the term…
Abstract
A polished glass disk medium substrate suitable for use as a substrate for a hard disk, a hard disk containing the substrate and methods for making the substrate. The substrate containing glass forming raw materials may be formed so as to have a Young's modulus of 110 or higher.
Claims35
A polished glass ceramic disk medium substrate comprising crystalline and amorphous phases formed of a mixture of glass forming raw materials comprising
- about 45% to about 60% by weight SiO2;
- about 5% to about 20% by weight Al2O3;
- about 9% to about 25% by weight MgO;
- about 0.1% to about 12% by weight TiO2;
- about 0.1% to about 12% by weight Li2O;
- and
- about 5% to about 22% by weight ZnO,
- wherein said glass substrate has a Young's modulus of 110 GPa or higher.
5 more elements
A method of making a glass ceramic disk medium substrate comprising:
- heating glass forming raw materials to a temperature sufficiently high to melt the raw materials:
- forming a disk medium substrate;
- and
- crystallizing the disk medium substrate, wherein said crystallizing comprises heating the disk medium substrate to a temperature, T1, between about 500 and 680° C. to generate crystal nuclei;
- heating at a temperature, T2, between about 680 and about 800° C. to grow crystal nuclei;
- and cooling to obtain crystallized glass, wherein the glass forming raw materials comprise
- about 45% to about 60% by weight SiO2;
- about 5% to about 20% by weight Al2O3;
- about 9% to about 25% by weight MgO;
- about 0.1% about 12% by weight TiO2;
- about 0.1% to about 12% by weight Li2O;
- and
- about 5% to about 22% by weight ZnO,
- wherein said glass substrate has a Young's modulus of 110 GPa or higher.
11 more elements
Dependencies are inferred from the claim text.