Uniform small cell foams and a continuous process for making same
Assignee3M Innovative Properties Company
InventorsMark David Gehlsen, David Loren Vall, Craig Allen Perman, Bonnie Weiskopf Albrecht
Life of this patent
Estimating the term…
Abstract
A continuous method for making foams having uniform and/or small cell sizes and articles made with these foams are described. The method allows for adjusting or controlling cell size and cell size distribution by controlling temperature and/or blowing agent concentration. The foams feature small and/or uniform cell sizes and may be comprised of amorphous thermoplastic polymers, pressure sensitive adhesive compositions, and immiscible thermoplastic polymer compositions. A method for coextruding the foams is also described.
Claims15
A continuous method for making a foam material comprising:
- (1) mixing at least one amorphous thermoplastic polymeric material and at least one physical blowing agent in an apparatus having an exit shaping orifice at a temperature and pressure sufficient to form a melt solution wherein the blowing agent is uniformly distributed throughout the polymeric material;
- (2) reducing the temperature of the melt solution at the exit of the apparatus to an exit temperature that is less than 15° C. above the glass transition temperature of the neat polymeric material while maintaining the melt solution at a pressure sufficient to keep the blowing agent in solution;
- and
- (3) passing the solution through said exit shaping orifice and exposing the solution to atmospheric pressure, whereby the blowing agent expands causing nucleation and cell formation resulting in the melt solution foaming and solidifying at or about the time it exits the shaping orifice.
A continuous method for making a foam material comprising:
- (1) mixing at least one amorphous thermoplastic pressure sensitive adhesive polymeric material and at least one physical blowing agent in an apparatus having an exit shaping orifice at a temperature and pressure sufficient to form a melt solution wherein the blowing agent is uniformly distributed throughout the polymeric material;
- (2) reducing the temperature of the melt solution at the exit of the apparatus while maintaining the melt solution at a pressure sufficient to keep the blowing agent in solution;
- and
- (3) passing the solution through said exit shaping orifice and exposing the solution to atmospheric pressure, whereby the blowing agent expands causing nucleation and cell formation resulting in the melt solution foaming and solidifying at or about the time it exits the shaping orifice.
Dependencies are inferred from the claim text.