pH adjustment of a strengthening melt for use in strengthening glass substrates

Abstract

A method of adjusting the pH of a strengthening melt for use in strengthening glass substrates, e.g., glass disk substrates for use in data storage devices. A non-particle-forming acid is added to the strengthening melt to lower the pH of the strengthening melt to ≦8. The acid is added while the strengthening melt is in a molten state and selected to avoid particle formation. Nitric acid, for example, is non-particle-forming with respect to nitrate based strengthening melts such as potassium nitrate and/or sodium nitrate. A base, e.g., sodium hydroxide, may be added if the pH of the strengthening melt falls below 5. Strengthening melts are subject to pH shift that can cause glass substrates strengthened therein to etch, creating pits on the substrate surface. Glass disk substrates treated in the pH adjusted strengthening melt are essentially free from such pits, as well as contamination caused by particle formation.