Highly compressible iron powder
AssigneeKawasaki Steel Corporation
InventorsYukiko Ozaki, Masateru Ueta, Naomichi Nakamura
Life of this patent
Estimating the term…
Abstract
A highly compressible iron powder for powder metallurgy has an optimized particle size distribution. The Vickers microhardness of the particles that do not pass through the sieve having the nominal opening of 150 μm is controlled to be at most about 110. The iron powder is suitable for production of magnetic parts having high magnetism and mechanical parts having high mechanical strength.
Claims8
A highly compressible iron powder for powder metallurgy comprising, on the basis of mass percent of fractions after sieve classification using sieves defined in Japanese Industrial Standard (JIS) Z 8801-1:00 (Edition 2000):
- substantially 0% particles that do not pass through a sieve having a nominal opening of 1 mm;
- more than 0% to about 45% or less particles that pass through a sieve having a nominal opening of 1 mm and do not pass through a sieve having a nominal opening of 250 μm;
- about 30% and more to about 65% or less particles that pass through a sieve having a nominal opening of 250 μm and do not pass through a sieve having a nominal opening of 180 μm;
- about 4% and more to about 20% or less particles that pass through a sieve having a nominal opening of 180 μm and do not pass through a sieve having a nominal opening of 150 μm;
- and
- 0% and more to about 10% or less particles that pass through a sieve having a nominal opening of 150 μm,
- wherein the Vickers microhardness of the particles that do not pass through the sieve having the nominal opening of 150 μm is at most about 110.
A highly compressible iron powder for powder metallurgy comprising, on the basis of mass percent of fractions after sieve classification using sieves defined in Japanese Industrial Standard (JIS) Z 8801-1:00 (Edition 2000):
- substantially 0% particles that do not pass through a sieve having a nominal opening of 1 mm;
- more than 0.0% to about 2% or less particles that pass through a sieve having a nominal opening of 1 mm and do not pass through a sieve having a nominal opening of 180 μm;
- about 30% and more to about 70% or less particles that pass through a sieve having a nominal opening of 180 μm and do not pass through a sieve having a nominal opening of 150 μm;
- and
- about 20% and more to about 60% or less particles that pass through a sieve having a nominal opening of 150 μm,
- wherein the Vickers microhardness of the particles that do not pass through the sieve having the nominal opening of 150 μm is at most about 110.
Dependencies are inferred from the claim text.