Nickel-metal hydride storage battery

Abstract

The nickel-metal hydride storage battery of this invention includes a nonsintered nickel electrode using, as a positive electrode active material, nickel hydroxide including, as a solid-solution element, at least one element Q selected from the group consisting of Mn, Al, Y, Yb and Co; and a pasted hydrogen-absorbing alloy electrode using, as a negative electrode active material, a hydrogen-absorbing alloy represented by a composition formula, TiaVbNicMd, in which a+b+c=100; 15≦a≦45; 35≦b≦75; 5≦c≦25; 0<d≦7; and M is at least one element selected from the group consisting of Cr, Mn, Mo, Nb, Ta, W, La, Ce, Y, Mm, Co, Fe, Cu, Si, Al, B, Zr and Hf, and the ratio in capacity between the nonsintered nickel electrode and the pasted hydrogen-absorbing alloy electrode is 1:1.1 through 1:1.8. As a result, the invention provides a nickel-metal hydride storage battery having large battery capacity and a long cycle life.