The present invention aims at providing a sophisticated segregation reducing technique which a conventional technique cannot achieve by finding the relationship between the casting structure and the segregation of components at the time of solidification and the heat treatment conditions. That is, the present invention aims at providing material for shadow masks which exhibits excellent quality with respect to streaks. A material for a shadow mask of the present invention is formed of a casting slab for preparing the shadow mask which comprises an Ni—Fe alloy containing 30 to 45% of Ni. The casting slab has a cast structure comprising a columnar crystal and/or a chill crystal in an amount of 99% or more. In particular, it is preferred that the casting slab contains no equiaxed crystal. To this end, such casting slab is prepared by a continuous casting method in which casting operation is carried out with no electromagnetic stirring and with maintaining a melt temperature of the non-solidificated part in the slab at a temperature equal to or more than the liquidus thereof. Further, the resultant slab is subjected to a heat treatment at a temperature for a time such that the K value becomes 150 μm or more, to thereby diffuse the segregation of Ni.
A casting slab for producing a shadow mask comprising a Ni—Fe alloy containing 30-45% of Ni, wherein the casting slab comprises a columnar crystal and/or a chill kcrystal in an amount of 99% or more of the casting structure and a K value equal to or more than 150 μm, thus exhibiting excellent quality with respect to streaks.
A continuous casting slab for producing a shadow mask characterized in that the casting slab is subjected to the heat treatment such that the K value becomes equal to or more than 150 μm, the casting slab comprises a Ni—Fe alloy containing 30-45% of Ni, and the casting slab comprises a columnar crystal and/or a chill crystal in an amount of 99% or more of the casting structure thus exhibiting excellent quality with respect to streaks.
A slab for producing a shadow mask comprising a Ni—Fe alloy containing 30-45% of Ni, wherein the standard deviation of Ni segregation in a slab is set to not more than 0.07 mass % and the slab has a K value of at least 150 μm, thus exhibiting the excellent quality with respect to streaks.
A method for producing shadow mask material characterized in that a shadow mask slab which comprises a Ni—Fe alloy containing 30-45% Ni, has a K value of at least 150 μm, and exhibits a standard deviation of Ni segregation on a slab of not more than 0.07 mass % is subjected to hot rolling, cold rolling and annealing thus producing the shadow mask material exhibiting excellent quality with respect to streaks.
A method for producing a slab for producing a shadow mask comprising a Ni—Fe alloy containing 30-45% of Ni, wherein a continuous casting slab is subjected to heat treatment at a given temperature and for a given time to set the K value to equal to or more than 150 μm so that the standard deviation of Ni segregation in the continuous casting slab becomes equal to or less than 0.07 mass % thus exhibiting the excellent quality with respect to streaks.
A method for producing shadow mask material comprising a Ni—Fe alloy containing 30-45 % of Ni, wherein, after continuous casting, a heat treatment is performed at a given temperature and for a given time such that the K value becomes equal to or more than 150 μm so as to make the standard deviation of Ni segregation in the continuous casting slab to equal to or less than 0.07 mass % and thereafter, the continuous casting slab is subjected to hot rolling, cold rolling and annealing thus producing the shadow mask material exhibiting excellent quality with respect to streaks.
Dependencies are inferred from the claim text.