US 6,618,537 B2Granted
Optical waveguide structures and methods of fabrication
AssigneeApplied WDM, Inc.
InventorsHenryk Temkin, Rudolf Feodor Kazarinov
Life of this patent
Estimating the term…
Abstract
Methods of fabricating solid state optical waveguide structures comprising a doped silicon dioxide core layer sandwiched between lower and upper doped silicon dioxide cladding layers on a silicon substrate. The core and upper cladding layers are deposited using a plasma enhanced CVD process. The core layer is patterned to define one or more waveguide cores. The lower cladding layer is preferably also deposited using a plasma enhanced CVD process but alternatively may be formed by thermal oxidation.
Claims18
A method of fabricating an optical waveguide structure, comprising:
- forming on a silicon substrate an optical waveguide core between lower and upper cladding layers of silicon oxide, each of said core and said lower and upper cladding layers formed by plasma enhanced chemical vapor deposition from silicon, oxygen and dopant containing atmospheres, deposition of said lower and upper cladding layer utilizing boron and phosphorous sources;
- annealing the waveguide core and the lower cladding layer such that the waveguide core is converted to optical quality glass, and forming the upper cladding layer by a succession of alternating deposition and annealing steps to conformally cover said waveguide core, to produce a waveguide structure such that said core has a higher refractive index than the refractive indices of each of the lower and upper cladding layers sufficient to enable waveguiding of optical signals introduced into said core.
A method of fabricating an optical waveguide structure comprising an optical waveguide core between lower and upper cladding layers of silicon oxide, comprising;
- forming said core and said lower and upper cladding layers by plasma enhanced chemical vapor deposition from silicon, oxygen and dopant containing atmospheres, said dopant containing atmosphere for deposition of said lower and upper cladding layers including both boron and phosphorous sources;
- annealing the waveguide core and the lower cladding layer such that the waveguide core is converted to optical quality glass, and forming the upper cladding layer by a succession of alternating deposition and annealing steps to conformally cover said waveguide core, to produce a waveguide structure such that said core has a refractive index about 0.01 to 0.014 higher than the refractive index of said upper cladding layer, and said lower cladding layer has a refractive index substantially equal to that of said upper cladding layer, the difference in the refractive index of said core relative to that of said upper and lower cladding layers enabling waveguiding of optical signals introduced into said core, and wherein
- said lower and upper cladding layers provide optical confinement within the waveguide structure of optical signals introduced into said core.
A method of fabricating an optical waveguide structure comprising:
- depositing on a silicon substrate by plasma enhanced chemical vapor deposition from a silicon, oxygen and dopant containing atmosphere, a lower cladding layer having a refractive index substantially equal to that of thermal oxide;
- depositing on said lower cladding layer by plasma enhanced chemical vapor deposition from a silicon, oxygen and dopant containing atmosphere, a core layer having a refractive index higher than that of fused silica;
- patterning said core layer to configure an optical waveguide core;
- depositing on said lower cladding layer by plasma enhanced chemical vapor deposition from a silicon, oxygen and dopant containing atmosphere, an upper cladding layer overlying said optical waveguide core;
- said upper cladding layer having a refractive index substantially equal to that of fused silica;
- annealing said lower cladding layer and said optical waveguide core to convert the waveguide core to optical quality glass, and forming the upper cladding layer by a succession of alternating deposition and annealing steps to conformally flow said upper cladding layer over said optical waveguide core enabling waveguiding of optical signals along and substantially confined within said waveguide core.
3 more elements
A method of fabricating an optical waveguide structure comprising an optical waveguide core between lower and upper cladding layers of silicon oxide, comprising:
- forming said lower cladding layer, said core and said upper cladding layer by plasma enhanced chemical vapor deposition from silicon, oxygen and dopant containing atmospheres, deposition of said lower and upper cladding layer utilizing boron and phosphorous dopant sources, and said deposited core comprising a stoichiometric composition silicon dioxide waveguide core having a refractive index of substantially 1.446;
- annealing the waveguide core and the lower cladding layer such that the waveguide core is converted to optical quality glass, and forming the upper cladding layer by a succession of alternating deposition and annealing steps to conformally cover said waveguide core, the dopant concentrations in said lower cladding layer and said upper cladding layer selected such that the refractive index of said core is greater than about 0.01 higher than the refractive index of said upper and lower cladding layers enabling waveguiding of optical signals alone and substantially confined within said core.
A method of fabricating an optical waveguide structure comprising an optical waveguide core between lower and upper cladding layers of silicon oxide, comprising:
- forming said lower cladding layer, said core and said upper cladding layer by plasma enhanced chemical vapor deposition from silicon, oxygen and dopant containing atmospheres,
- the atmosphere for depositing each of the lower and upper cladding layers including both boron and phosphorous dopant sources such that said deposited layers each has a refractive index substantially equal to that of thermal oxide;
- the atmosphere for depositing said waveguide core including a phosphorous dopant source such that said deposited waveguide core has a refractive index greater than about 0.01 higher than that of thermal oxide;
- annealing the waveguide core and the lower cladding layer such that the waveguide core is converted to optical quality glass, and forming the upper cladding layer by a succession of alternating deposition and annealing steps to conformally cover said waveguide core,
- said deposited lower and upper cladding layers each having a thickness to optically confine optical signals introduced into said waveguide core within the waveguide structure comprising said lower and upper cladding layers and said waveguide core.
2 more elements
A method of fabricating an optical waveguide structure on a silicon substrate, said waveguide structure comprising an optical waveguide core between lower and upper cladding layers of silicon oxide, comprising:
- forming said lower cladding layer by plasma enhanced chemical vapor deposition from silicon, oxygen, boron, and phosphorous containing atmosphere at a temperature within a selected range;
- forming said core by patterning an intermediate layer on said lower cladding layer by plasma enhanced chemical vapor deposition from a silicon, oxygen, and phosphorous containing atmosphere at a temperature within said selected range;
- annealing said lower cladding layer and said core to convert said core to optical quality glass;
- forming the upper cladding layer by a succession of alternating deposition and annealing steps, said deposition steps each comprising plasma enhanced chemical vapor deposition from a silicon, oxygen, boron, and phosphorous containing atmosphere at a temperature within said selected range to conformally flow said upper cladding layer around upper and side surfaces of said waveguide core;
- the phosphorous doped core having a refractive index greater than about 0.01 higher than the refractive index of the lower cladding layer and the refractive index of the upper cladding layer;
- and
- said deposited lower cladding layer providing optical isolation of said waveguide core from said silicon substrate and said upper cladding layer optically confining within the waveguide structure, optical signals introduced into said waveguide core.
4 more elements
Dependencies are inferred from the claim text.