Molding composition of siloxane capable of extending mold lifetime
OwnerWen-Chen Yanginventor
Life of this patent
Estimating the term…
Abstract
The present invention provides the molding composition of siloxane, which is capable of extending mold lifetime where inhibitors alkene or acetylene polymerization are mixed in the molds composed of siloxane. The inhibitors can effectively inhibit the release of alkene or acetylene when a resin containing an alkene or acetylene is poured into the molds which extends lifetime of molds composed of siloxane. The inhibitors are compounds containing primarily sulfur, wherein sulfur is the most effective.
Claims3
A curable silicone composition for making molds hardened using a hardening agent, comprising:
- a. trimethylsiloxyl end blocked polydimethylsiloxane having a viscosity of 100-1,000 cps at 25° C.;
- b. hydroxyl group end blocked polydimethylsiloxane having a viscosity of 5,000-100,000 cps at 25° C.;
- c. a filler;
- d. a surface treatment agent of the filler;
- and,
- e. an alkene or acetylene polymerization inhibitor selected from the group consisting of:
- (i) sulfur;
- (ii) disulfides having a formula R′—S—S—R″, where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- (iii) organic tin containing sulfur having a formula [R2SnS]3, where R is selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- and
- (iv) organic tin containing sulfur having a formula R2′Sn(SR″)2 where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms.
A curable silicone composition for making molds hardened using a hardening agent, comprising:
- a. trimethylsiloxyl end blocked polydimethylsiloxane having a viscosity of 100-1,000 cps at 25° C.;
- b. hydroxyl group end blocked polydimethylsiloxane having a viscosity of 5,000-100,000 cps at 25° C.;
- c. precipitated silicone dioxide having a surface area of 50-250 m2/g;
- d. hexamethyldisilazane;
- and
- e. an alkene or acetylene polymerization inhibitor selected from the group consisting of;
- (i) sulfur;
- (ii) disulfides having a formula R′—S—S—R″, where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- (iii) organic tin containing sulfur having a formula [R2SnS]3;
- where R is selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- and
- (iv) organic tin containing sulfur having a formula R2′Sn(SR″)2, where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms.
A composition for making molds to which a hardening agent is added, the composition being formed by a process comprising the steps of:
- a. preparing a curable silicone composition by combining trimethylsiloxyl end blocked polydimethylsiloxane having a viscosity of 100-1,000 cps at 25° C., hydroxyl group end blocked polydimethylsiloxane having a viscosity of 5,000-100,000 cps at 25° C., hydroxyl group end blocked polydimethylsiloxane, and a filler;
- and,
- b. adding to said curable silicone composition an alkene or acetylene polymerization inhibitor selected from the group consisting of;
- (i) sulfur;
- (ii) disulfides having a formula R′—S—S—R″, where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- (iii) organic tin containing sulfur having a formula [R2SnS]3, where R is selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms;
- and
- (iv) organic tin containing sulfur having a formula R2′Sn(SR″)2, where R′ and R″ are each independently selected from a group of monovalent hydrocarbon radicals having from one to forty carbon atoms.