Fe alloy material for thixocasting and method for heating the same
AssigneeHonda Giken Kogyo Kabushiki Kaisha
InventorsMasayuki Tsuchiya, Hiroaki Ueno
Life of this patent
Estimating the term…
Abstract
A thixocast Fe-based alloy material is provided, from which a cast product having mechanical properties uniform over the whole thereof can be produced. The Fe-based alloy material comprises 1.8% by weight≦C≦2.5% by weight, 1.0% by weight≦Si≦3.0% by weight, 0.1% by weight≦Mn≦1.5% by weight, 0.5% by weight≦Ni≦3.0% by weight, and as the balance, iron (Fe) including inevitable impurities. The eutectic crystal amount Ec is in a range of 10% by weight<Ec<50% by weight.
Claims4
A thixocast Fe-based alloy material comprising
- 1.8% by weight≦C≦2.5% by weight
- 1.0% by weight≦Si≦3.0% by weight
- 0.1% by weight≦Mn≦1.5% by weight
- 0.5% by weight≦Ni≦3.0% by weight, and
- as the balance, iron (Fe) including inevitable impurities,
- wherein an amount Ec of eutectic crystal consisting of Fe and C is in a range of 10% by weight<Ec<50% by weight.
A thixocast Fe-based alloy material comprising
- 1.8% by weight≦C≦2.5% by weight
- 1.0% by weight≦Si≦3.0% by weight
- 0.8% by weight≦Mn≦1.5% by weight, and
- as the balance, iron (Fe) including inevitable impurities,
- wherein an amount Ec of eutectic crystal consisting of Fe and C is in a range of 10% by weight<Ec<50% by weight.
A thixocast Fe-based alloy material, comprising carbon (C) of a content in a range of 1.8% by weight≦C≦2.5% by weight, silicon (Si) of a content in a range of 1.0% by weight≦Si≦3.0% by weight, manganese (Mn) of a content in a range of 0.6% by weight≦Mn≦1.5% by weight, at least one of nickel (Ni) of a content in a range of 0.2% by weight≦Ni≦3.0% by weight and titanium (Ti) of a content in a range of 0.05% by weight≦Ti≦0.6% by weight, the total sum of the Mn content, the Ni content and the Ti content being equal to or larger than 0.8% by weight (Mn+Ni+Ti≧0.8% by weight), and the balance being iron (Fe) including inevitable impurities, wherein an amount of eutectic crystal consisting of Fe and C is in a range of 10% by weight<Ec<50% by weight.
Dependencies are inferred from the claim text.